The invention relates to a formula for light material, in particular to a formula for light body composite material. The formula comprises the following weight parts materials: light burned magnesium 100, 95 - 115, a mixture of plant straw powder 20 - 45. The mixture consists of the following parts by weight: 40 to 45 materials of magnesium chloride, three sodium phosphate 0.3 - 0.5, 0.2 - 0.3 oxalic acid and sulfuric acid, 0.8 - 1 weight 0.15 - 0.25 hydrogen peroxide. When the composite material is processed into various forms of plates, a fixed block is arranged at the edge thereof. The invention has the advantages of light weight, high strength, good toughness, waterproof, heat insulation, heat preservation, etc., and the installation and maintenance are quick and convenient.
【技术实现步骤摘要】
本专利技术涉及一种轻质材料,特别涉及一种轻体复合材料的配方和预制件。
技术介绍
目前,市场轻质材料产品所用的材料为水泥混合砂浆,这种材料生产的产品的缺点是体质重、脆性大、易损坏、施工不方便,因此,便急需一种新型材料来取代。
技术实现思路
本专利技术的目的是提供一种轻体复合材料预制件,解决现有材料的体质重、脆性大、易损坏、施工不方便等技术问题。本专利技术的技术方案本专利技术轻体复合材料的配方,包括下列重量份的材料组成轻烧镁粉100份、混合液95-115份、植物秸杆粉20-45份。其中,混合液包括下列重量份的材料组成氯化镁40-45份、磷酸三钠0.3-0.5份、草酸0.2-0.3份、硫酸压铁0.8-1.0份、双氧水0.15-0.25份。用上述复合材料加工成各种形式的板材后,在其边缘设置有固定块。本专利技术的有益效果本配方生产的复合材料与现有技术相比具有轻质高强、韧性好、防水、隔热保温等性能,安装、维护方便快捷。四附图说明无五具体实施例方式轻体复合材料预制件如下包括下列重量份的材料组成轻烧镁粉100份、混合液95-115份、植物秸杆粉20-45份;其中,混合液包括下列重量份的材料组成氯化镁40-45份、磷酸三钠0.3-0.5份、草酸0.2-0.3份、硫酸压铁0.8-1.0份、双氧水0.15-0.25份。用上述复合材料加工成各种形式的板材后,在其边缘设置有固定块。实施例1,轻体复合材料预制件如下轻烧镁粉100份、混合液95份、植物秸杆粉20份;其中,混合液包括下列重量份的材料组成氯化镁40份、磷酸三钠0.3份、草酸0.2份、硫酸压铁0.8份、双氧水0.15份。实施例 ...
【技术保护点】
一种轻体复合材料预制件,其特征是轻体复合材料包括下列重量份的材料组成:轻烧镁粉100份、氯化镁40-45份、磷酸三钠0.3-0.5份、草酸0.2-0.3份、硫酸压铁0.8-1.0份、双氧水0.15-0.25份、植物秸杆粉20-45份;用上述复合材料加工成各种形式的板材后,在其边缘设置有固定块。
【技术特征摘要】
【专利技术属性】
技术研发人员:王怀堂,卢庆兰,王克民,
申请(专利权)人:东营市星河新型建材有限责任公司,
类型:发明
国别省市:37[中国|山东]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。