A plant growing concrete, water, cement, coarse aggregate, additive and stirring, the ratio between them is: 1: 2.8 to 3.3: 12 to 18: 0.01 to 0.03, with 425 grade cement, coarse aggregate grain size is 2cm ~ 4cm. A new formulation of the invention uses concrete materials, the use of new construction methods, made of porous concrete, at the same time by strong alkaline additives and concrete, using specially selected plant seeds, plants can make in concrete or through concrete and growth. The invention has the advantages of simple manufacture, commercial and large-scale production, and can be applied to the construction works of the parking lot, the sidewalk, the roof and various vertical elevations.
【技术实现步骤摘要】
本专利技术涉及一种混凝土。特别是能用于停车厂、屋顶等处绿化的混凝土。
技术介绍
在河道护坡、停车厂、人行道、屋顶以及各种垂直立面施工过程中,采用普通混凝土,这些混凝土侧重于强度要求,其表面不可能生长花草,不仅景观单调,且不利于生态平衡,已有的绿化技术是利用藤本植物进行绿化,这种绿化方法只适用于低矮边坡,且难以尽快完全覆盖坡面。
技术实现思路
本专利技术的目的就是要提供一种制作简单、可实现商品化、规模化生产的特别是能用于停车厂、屋顶等处绿化的植生混凝土。本专利技术的技术方案是这样得以实现的一种植生混凝土,其特点是它由水、水泥、粗骨料、添加剂搅拌而成,它们之间的用量比例(重量比)是1∶2.8~3.3∶12~18∶0.01~0.03,采用水泥标号425#以上,粗骨料的粒径为2cm~4cm。本专利技术利用混凝土组成材料的新配比,使用新的施工方法,制造出混凝土的大孔隙,同时通过添加剂中和混凝土的强碱性,采用专选的植物种子,使植物能够在混凝土中或者透过混凝土而生长。本专利技术可用在停车厂、人行道、屋顶以及各种垂直立面施工工程上,在保证构筑物设计强度前提下,基本保持原有生态环境,相对普通混凝土来说,能够大大提高绿化量,营造良好的生态环境,是可持续发展的工程技术保证措施之一。具体实施例方式实施例1将土壤耕平、播种施肥,再在其上支模,然后在模板上浇筑已搅拌均匀的植生混凝土,植生混凝土是由水、水泥、粗骨料、添加剂搅拌而成,它们之间的用量比例(重量比)是1∶3∶13∶0.018,采用水泥标号为425#以上,粗骨料的粒径为4cm;进行养护后不多久混凝土下的土壤里的草就穿过混凝土的 ...
【技术保护点】
一种植生混凝土,其特征在于:它是由水、水泥、粗骨料、添加剂搅拌而成,它们之间的用量重量比是:1∶2.8~3.3∶12~18∶0.01~0.03,水泥标号为425#以上,粗骨料的粒径为2cm~4cm。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。