氮化硅陶瓷细长工件的生产工艺技术制造技术

本发明专利技术涉及氮化硅Ｓｉ↓［３］Ｎ↓［４］陶瓷细长工件生产工艺技术。本发明专利技术的专门工艺技术主要是将细长工件合理设计成若干短段（图１：件１件２件３）进行成型、预烧结、机加工、组合、烧结等进行生产。并特别提出，在短段组合中将与短段原料配方一致的糊状混合物（４）充填粘合在组合间隙、平面接合处、平面接合处的外圆（外表面）后（图３），与组合成的整体工件一并烧结，糊状混合物经最终烧结后与各短段成焊接性质结合一体，溶入完整的氮化硅陶瓷细长工件中，确保低成本、生产出高成品率的产品。

Production technology of silicon nitride ceramic slender workpiece

The present invention relates to silicon nitride Si: the production technology of 3 N: 4 Ceramic slender workpiece. The special process technique of the invention is that the slender workpiece is rationally designed into a plurality of short segments (Figure 1: 1 pieces, 2 pieces, 3 pieces) for molding, pre sintering, machining, combination, sintering and the like. And in particular, the paste mixture formula of raw materials consistent with the short segment in combination with short segment (4) filling adhesive in combined gap, planar junction, the junction of the outer circle plane (outer surface) after (Figure 3), and the whole piece together into paste mixture by sintering and sintering the final the short section combined properties of welding, silicon nitride ceramic slender piece into complete, to ensure low cost and high yield production.

【技术实现步骤摘要】

本专利技术涉及氮化硅Si3N4陶瓷细长工件(L/D＞10)生产工艺技术。其中L-工件的长度；D-工件的直径(或边长)。
技术介绍
氮化硅陶瓷细长工件在生产过程中，由于1、素坯成型必须要大型专用设备，企业投资大；2、硅粉末或氮化硅粉末本身之间及与它们配料之间的结合强度很低，素坯成型一次性达到图纸尺寸和形状的成品率很低；3、即使使用成本高的专用成型设备，素坯成型后的机械加工工艺也将十分困难，成品率也很低；4、再即使素坯能够成型并进行机械加工完毕后，最终整根细长氮化硅半成品在氮化烧结炉中变形极大，而且众所周知的，成品率极低。综上因素，企业无法接受上述如此高昂成本的氮化硅陶瓷细长工件产品生产。
技术实现思路
鉴于以上情况，本专利技术提供氮化硅陶瓷细长工件在成型、机加工、烧结等工艺过程的专门工艺技术以解决生产设备成本高，质量无法保证，成品率低下的难题。本专利技术主要工艺技术是将细长工件合理设计成若干短段进行成型、加工、组合充填粘结、成品烧结等生产过程。并特别提出，在短段组合中将与短段原料配方一致的糊状混合物充填粘合在组合间隙、平面接触处、平面接触处外园(外表面)后，与组合成的整体工件一并烧结，本文档来自技高网...

【技术保护点】
一种新的氮化硅陶瓷细长工件的生产工艺技术。由素坯成型－予烧结－机械加工－组合充填糊状混合物－烧结－深加工等工序组成。其特征是首先把细长工件合理设计成若干短段，进行素坯成型、予烧结、机械加工等工序直至组合成型，最后成品烧结、深加工。

【技术特征摘要】