低收缩高抗渗微晶材料制造技术

本发明专利技术涉及一种低收缩高抗渗微晶材料，由凝聚硅胶、硫铝酸盐微粉、多环芳香族磺酸盐减水剂、聚丙烯抗裂防渗纤维组成；其质量百分数是：凝聚硅胶１８％－５８％，硫铝酸盐微粉３０％－７０％，多环芳香族磺酸盐减水剂７％－１２％，聚丙烯抗裂防渗纤维５％－１０％；本发明专利技术的有益效果是：不但在指标上全部符合国家行业标准ＪＣ４７４－１９９９且有较大的富裕，特别是抗渗能力大于３．５ＭＰａ，这是一般防水材料都难以达到的指标。

Low shrinkage and high permeability microcrystalline material

The invention relates to a low shrinkage and high impermeability of microcrystalline materials by condensation, silica gel, sulphoaluminate powder, polycyclic aromatic sulfonate superplasticizer and polypropylene fiber on crack resistance and impermeability; the mass percentage is: condensed silica gel 18% - 58%, 30% - 70% of sulphoaluminate powder, polycyclic aromatic sulfonate superplasticizer 7% - 12% polypropylene cracking impervious fiber 5% - 10%; the beneficial effect of the invention is: not only in the index all meet the national standard JC474 - 1999 and greater prosperity, especially the impermeability of more than 3.5MPa, it is generally difficult to achieve the target of waterproof material.

【技术实现步骤摘要】

本专利技术涉及一种建筑防水材料，尤其涉及一种低收缩高抗渗微晶材料。
技术介绍
建筑材料在拌和时加水的主要作用是参加水化反应，反应的结果是使水泥产生一种能把搅拌成均匀状态的砂、石、粉料等建筑材料凝结在一起的胶凝物质---水化硅酸钙。参与水化反应所需的水有几种存在形式，其中结晶水的水份以OH-离子状态存在，与水化反应后的晶体有着固定的搭配，其余的如游离水，凝胶水以及弱结晶水会随着时间和水化石的硬化过程逐渐蒸发，最后在水化石中留下毛细孔或微裂缝。如果加水过多，在水份蒸发过程会直接产生收缩裂缝。所以控制参与水化反应的加水量将是建筑防水成败的关键。由于微晶材料的细微颗粒，与同质量的较大粒径的材料相比，其表面积就较大，在搅拌时就需要较多的水来湿润表面。在水化过程中水泥会释放出氧化钙，遇水生成氢氧化钙，同时放出热量，热量的积聚会在水泥砂浆或混凝土中形成体积膨胀，当施工完毕，这些热量在向周围环境散热时会引起体积收缩，这就是微裂缝产生的原因。如果水泥中氧化钙含量过多，水泥的安定性就不合格，用到建筑上就会产生大量的裂缝，造成建筑物的渗漏。由于水泥砂浆和混凝土在本质上可看作是由不同粒径的颗粒堆积而成的本文档来自技高网...

【技术保护点】
一种低收缩高抗渗微晶材料，由凝聚硅胶、硫铝酸盐微粉、多环芳香族磺酸盐减水剂、聚丙烯抗裂防渗纤维组成；其质量百分数是：凝聚硅胶１８％－５８％，硫铝酸盐微粉３０％－７０％，多环芳香族磺酸盐减水剂７％－１２％，聚丙烯抗裂防渗纤维５％－１０％。

【技术特征摘要】

【专利技术属性】
技术研发人员：李行健，李晓蓉，
申请(专利权)人：上海宏恩科技发展有限公司，
类型：发明
国别省市：31[中国|上海]