一种高强度电瓷配方组成比例

本发明专利技术公开了一种超高强度电瓷配方，其所包含的组份及重量百分比为：水曲柳粘土８～１２％；长石粉９～１３％；烧矾石粉３７～４７％彰武粘土６～１０％；法库粘土５～１０％；宽城粘土４～８％；宝丰粘土５．５～８．５％；永吉粘土４～８％；改性膨润土０．５～１．５％。按照本发明专利技术配方生产的电瓷产品的各项性能已达到并超过ＧＢ８４１１中Ｖ类瓷标准，特别是抗折强度可达到１６５～１７０Ｍｐａ（无釉）或２２１～２３１Ｍｐａ（有釉），完全可以满足２２０～１０００ＫＶ输变电系统的要求，是一种生产超高强度电瓷的新型配方，添补了我国此类产品的空白。

High strength electric porcelain formula

The invention discloses an ultra high strength electroceramic composition, which includes the components and the weight percentage: 8 to 12% ash clay feldspar powder; 9 ~ 13%; 37 ~ 47% alum powder burning Zhangwu clay from 6 to 10%; 5 to 10% clay Faku; Kuancheng clay 4 ~ 8%; 5.5 ~ Baofeng clay 8.5% Yongji 4 ~ 8%; clay; modified bentonite from 0.5 to 1.5%. According to the performance of the production recipe of the invention of porcelain products has reached more than GB8411 in the class V standard, especially the flexural strength can reach 165 ~ 170Mpa (unglazed) or 221 ~ 231Mpa (glazed), can fully meet the 220 ~ 1000KV power transmission system, is a new formula produced by students high strength porcelain, fills the blank of such products in china.

【技术实现步骤摘要】

本专利技术属于电瓷
，具体涉及一种生产超高强度电瓷的配方。
技术介绍
随着电力事业的迅速发展，电压等级的不断提高，我国对用于高压和超高压输变电系统的瓷绝缘子的要求也越来越高，而现有瓷绝缘子的瓷质性能已经达不到要求，特别是瓷质的抗折强度，一般仅在140Mpa～160Mpa水平上，根本不能满足220～1000KV输变电系统的要求。目前，此类产品就只能靠进口来满足国内的需求，这样，不但造成资金的大量流失，而且还严重地阻碍了电力事业的发展。二
技术实现思路
本专利技术的目的是提供一种电瓷配方，应用该配方生产的电瓷产品绝缘性能好、机械强度高。本专利技术一种超高强度电瓷配方，所包含的组份及重量百分比为水曲柳粘土8～12％ 长石粉9～13％烧矾石粉37～47％彰武粘土6～10％法库粘土5～10％ 宽城粘土4～8％宝丰粘土5.5～8.5％ 永吉粘土4～8％改性膨润土0.5～1.5％。本专利技术的制作工艺与其它电瓷的制作工艺基本相同，采用湿成型，工艺流程如下一次配料→湿法球磨→二次配料→湿法球磨→过筛除铁→榨泥→陈腐→真空挤制→阴干→修坯→光坯阴干→烘干→上釉上砂→装窑→培烧→瓷检→切割研本文档来自技高网...

【技术保护点】
一种超高强度电瓷配方，其特征是：所包含的组份及重量百分比为：水曲柳粘土８～１２％；长石粉９～１３％；烧矾石粉３７～４７％；彰武粘土６～１０％；法库粘土５～１０％；宽城粘土４～８％；宝丰粘土５．５～８．５％；永吉粘土４～８％；改性膨润土０．５～１．５％。

【技术特征摘要】

【专利技术属性】
技术研发人员：路延枢，路世伟，
申请(专利权)人：抚顺高科电瓷电气制造有限公司，
类型：发明
国别省市：21[中国|辽宁]