The invention discloses a resin adhesive for repairing oil medium concrete, its composition and ratio (by weight): epoxy resin curing agent: 100, 40 to 50 copies, accelerator: 2 ~ 6 copies, coupling agent: 2 ~ 6, 10 ~ 50, thinner: oil absorbing resin: from 0 to 50, 0 to 50 portions of PVC resin. The present invention is the resin adhesive adherend surface curing process can not only absorb the concrete surface reservoir, and to gradually spread to the adhesive layer, and forming a uniform whole, so as to achieve the adherend adhesive molecules and molecular maximum contact. The oil medium which has been penetrated into the concrete can be absorbed sufficiently by the material to be absorbed, and has high strength to be bonded with the concrete body.
【技术实现步骤摘要】
本专利技术涉及一种建筑材料,尤其涉及一种在油介质中修补混凝土的树脂胶粘剂。
技术介绍
国内对于地下构筑物裂缝的处理主要集中在渗漏水的方面,而对于渗漏油的处理至今尚无较好的治理方法,已成为堵漏专项技术的薄弱环节。用堵水的方法进行油质渗漏的修复,修复寿命为三个月左右。所以研制修复实际工程中油介质裂缝的特殊材料成为当前的关键所在。国内还没有从工艺理论上、材料上进行综合性、系统性研究的文献记载,是地下构筑物渗漏堵漏技术研究领域的一个空白点。
技术实现思路
针对已有技术存在的不足,本专利技术的目的在于提供一种用于油介质混凝土修补的树脂类胶粘剂,即一种与内部已吸足油性介质的混凝土产生良好粘结的改性树脂。本专利技术的专利技术目的是通过如下技术方案实现的一种油介质混凝土缺陷树脂修补材料,其组成及配比为(按重量份计)环氧树脂100份,固化剂40~50份,促进剂2~6份,偶联剂2~6份,稀释剂10~50份,吸油树脂0~50份,PVC树脂0~50份。所述固化剂选自改性胺类,如乙二胺、二乙烯三胺、三乙烯四胺、酰氨基胺等;所述稀释剂为含有反应活性环氧基的聚醚类稀释剂,如缩水甘油醚、环氧丙烷丁基醚等;所述促进剂为改性胺类环氧固化促进剂,如活性聚酰胺、改性芳香族胺等;所述吸油树脂为合成腈类聚合物,如PVC树脂等。为防止胶粘剂固化后吸收的油重新渗出而影响粘结效果,必须使胶粘剂固化层能与油具有良好的相容性。在改性树脂配方的基础上,加入了适当的吸油性活性填料来吸收被粘物表面油层。本专利技术对环氧树脂进行改性,使得其在吸油性、粘接性方面取得好的效果,使被粘物表面固化过程中不仅能吸收混凝土表面油 ...
【技术保护点】
一种油介质混凝土缺陷树脂修补材料,其组成及配比为:环氧树脂:100份,固化剂:40~50份,促进剂:2~6份,偶联剂:2~6份,稀释剂:10~50份,吸油树脂:0~50份,PVC树脂0~50份,以上份数均为重量份。
【技术特征摘要】
【专利技术属性】
技术研发人员:包朝亮,钟世云,张立华,叶岚,张敏,王秋蓉,
申请(专利权)人:上海宝冶工程技术有限公司,
类型:发明
国别省市:31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。