本发明专利技术公开了一种星光石的制备方法。该方法是将由钾长石６～１２份、钠长石６５～７２份、高温砂１０～１４份和球土１６～２０份组成的的重量份的原料经球磨研磨１０～２０小时、均化、造粒、陈腐１～２天、压制、干燥、烧成后制得。以本发明专利技术制得的星光石可完全取代微晶玻璃复合板，具有更强的耐磨性和更广的使用空间。版面细腻通透，层次分明，富有立体感。

Method for preparing star stone

The invention discloses a method for preparing starlight stone. This method is composed of 6 to 12 portions of potassium feldspar and albite 65 - 72, 10 to 14 portions of high temperature sand and soil ball 16 to 20 weight parts of the composition of raw materials by ball milling for 10 ~ 20 hours, homogenizing, granulation, 1 ~ 2 days old, pressing, drying and firing prepared. The star Shi Ke produced by the invention completely replaces the glass-ceramic composite board, and has stronger abrasion resistance and wider use space. The layout is exquisite and transparent, with distinct levels and rich three-dimensional feeling.

【技术实现步骤摘要】

本专利技术涉及无机硅酸盐
，具体地说，是。
技术介绍
通常，抛光砖产品，虽然厂家及其生产的品种繁多；但往往存在着下述问题1.色彩单调，往往是纯色砖，并且只有白色等几种颜色可以选择；2.砖的颗粒过于粗大，导致细腻不足，整体效果不自然、不流畅。
技术实现思路
本专利技术的目的在于，提供。为了实现上述的专利技术目的，本专利技术包含以下
技术实现思路
，其原料经球磨研磨10～20小时、均化、造粒、陈腐1～2天、压制、干燥、烧成后制得；所述的原料包含有以下重量的物质钾长石6～12份、钠长石65～72份、高温砂10～14份和球土16～20份。优选地，星光石包含以下重量的原料钾长石9份、钠长石68份、高温砂12份和球土18份。压制时，压机压力为35MPa，干燥温度为150℃，干燥水份为0.6wt％。在所述的造粒前，向原料中添加占原料总重量0.5～12.0％的硅酸锆，然后喷雾制粉。各原料的成份表可参见表1。表1各原料的成份表(wt％) 在造粒时，各种粒子的乳浊度为40～44、46～50、52～56、56～60。在造粒时，各种粒子的直径范围是0.8mm～1.6mm、1.6mm～2.0mm、2本文档来自技高网...

【技术保护点】
一种星光石的制备方法，其特征在于，包含以下步骤：原料经球磨研磨１０～２０小时、均化、造粒、陈腐１～２天、压制、干燥、烧成后制得；所述的原料包含有以下重量的物质：钾长石６～１２份、钠长石６５～７２份、高温砂１０～１４份和球土１６～２０份。