Including the production of raw materials, preparation, mold and method for baking pottery or porcelain container for electromagnetic oven, the utility model is characterized in that: in the preparation of raw materials and preparation of magnetic metal slurry, magnetic metal slurry by different melting point and thermal expansion coefficient of metal powder mixed with water, stir well prepared for the body; when embedding a layer of magnetic metal in the mold and the mold bottom mud; or between porcelain body and glaze layer bottom mold is buried in a layer of magnetic metal slurry. By adopting the method, the metal powder is mutually fused during the roasting process, and the metal powder is fused with the embryo, and the metal powder and the embryo are mutually fused and bonded into a whole, and the magnetic metal mud is roasted into a magnetic conducting metal layer. Therefore, not only the finished product rate is high, but also the magnetic conducting metal layer and the container body are fused and bonded into an integral body, and the expansion coefficient of the magnetic conductive metal layer and the body is basically the same.
【技术实现步骤摘要】
本专利技术涉及一种加热容器的制作方法，尤其是一种电磁炉用的陶器或瓷 器容器的制作方法。
技术介绍
目前现有技术，中国专利，专利号ZL200520055040.2，专利技术创造名称 一种电磁炉用的砂锅。经过配料、成型、干燥、焙烧等工艺流程制成，其主 要结构是锅体底部内包埋有盘形金属板；盘形金属板为不锈铁材料。存在 问题是应用方法制作的成品，成品率低，由于铁材料与陶瓷的材料的膨胀系数不同，容易产生盘形金属板与锅体分离，造成锅底破裂。
技术实现思路
本专利技术的目的是提供一种，它 不但成品率高，而且导磁金属层与本体熔融粘接成一体，导磁金属层与容器 本体的膨胀系数基本相同。本专利技术是这样实现的 一种电磁炉用的陶器容器的制作方法包括原料配 制、制坯胎、焙烧，其特殊之处在于在原料配制的同时，配制导磁金属泥 桨，导磁金属泥浆由不同熔点、膨胀系数金属粉和水混合、搅拌均匀配制而 成；在制坯胎时，在坯胎的坯胎底内包埋一层导磁金属泥浆；所述导磁金属粉由不锈钢粉、钨粉、铜粉、锌粉和陶土构成，其配比为 (重量百分比)不锈钢粉40 70% 钨粉 10 25% 铜粉10 25% 锌粉 5 ...
【技术保护点】
一种电磁炉用的陶器容器的制作方法包括原料配制、制坯胎、焙烧，其特征在于：在原料配制的同时，配制导磁金属泥浆，导磁金属泥浆由不同熔点、膨胀系数金属粉和水混合、搅拌均匀配制而成；在制坯胎时，在坯胎的坯胎底内包埋一层导磁金属泥浆；所述导磁 金属粉由不锈钢粉、钨粉、铜粉、锌粉和陶土构成，其配比为：（重量百分比）不锈钢粉４０～７０％钨粉１０～２５％铜粉１０～２５％锌粉５～１０％陶土５～１０％导磁金属粉∶水＝１∶１。
【技术特征摘要】
...