一种硅藻土填料及其制备方法技术

本发明专利技术公开了一种硅藻土填料及其制备方法，硅藻土填料，由下列组分按重量百分比组成：硅藻土８３～８７％，铁粉８～１２％，糠粉４～６％，将硅藻土、铁粉和糠粉混合后恒温干燥，去除水分；加入发泡剂和粘结剂，搅拌均匀，粉碎；用造粒机将粉碎的物料制成直径３～６ｍｍ的球形；将球形物料煅烧；煅烧过程中，将煤干燥磨成粉末，用空气喷射装置将煤粉末均匀喷洒在球形物料上煅烧后进行筛分，分级，即得。本发明专利技术硅藻土填料具有生物附着性更强，微生物附着性强、物种更丰富，比表面积更大，孔隙率更高、水处理设施更稳定、能耗更少，轻质耐磨的优点。

Diatomite filler and preparation method thereof

The invention discloses a diatomite filler and a preparation method thereof, diatomite filler comprises the following components by weight percentage: 83 to 87% diatomite iron powder was 8 ~ 12%, 4 ~ 6%, bran powder, diatomite, iron powder and bran powder after constant temperature drying, moisture removal; adding foaming agent and binder, mixing with, crushing; granulating machine will crush the materials into 3 ~ 6mm diameter spherical spherical material; calcination; calcination process, the coal powder drying, air injection device of coal powder spraying calcination in spherical material after sieving, grading, i.e.. The present invention has biological diatomite filler adhesion stronger, microbial adhesion strength, more species rich, larger surface area, higher porosity, water treatment facilities are more stable, less energy consumption, has the advantages of light wear.

【技术实现步骤摘要】

本专利技术涉及水处理领域，具体的说是一种用于水处理的硅藻土填 料及其制备方法。技术背景在水处理中影响处理质量的关键是填料的好坏，而填料同时也对 水处理的成本起到关键的作用，目前，国内传统滤池的填料，多为陶 瓷填料，存在比重大、孔隙率低、能耗大、处理设施不稳定等问题。
技术实现思路
本专利技术的专利技术目的为提供一种比表面积大、孔隙率高的硅藻土填料。实现上述专利技术目的的技术方案如下 一种硅藻土填料，由下列组分按重量百分比组成硅藻土 83 87%铁粉 8 12%糠粉 4 6% 本专利技术的另一目的为提供一种上述硅藻土填料的制备方法。 一种制备上述硅藻土填料的方法，包括下列步骤a. 将硅藻土、铁和糠混合后恒温干燥，去除水分；b. 加入发泡剂和粘结剂，搅拌均匀，粉碎；c. 用造粒机将粉碎的物料制成直径3 6mm的球形；d. 将球形物料煅烧；e. 煅烧过程中，将煤干燥磨成粉末，用空气喷射装置将煤粉末均 匀喷洒在球形物料上；f. 煅烧后进行筛分，分级，即得。制得的硅藻土填料外形呈球形粒状，表观颜色为灰色、灰褐或土 黄色，具体参数如下直径3 6mm 灼烧减量0.09±0.001%磨损率1.5本文档来自技高网...

【技术保护点】
一种硅藻土填料，由下列组分按重量百分比组成：硅藻土８３～８７％铁粉８～１２％糠粉４～６％。

【技术特征摘要】

【专利技术属性】
技术研发人员：徐伟文，严明，陈向文，林凤盛，
申请(专利权)人：温州宏泽环保科技有限公司，
类型：发明
国别省市：33[中国|浙江]