本发明专利技术公开了一种陶瓷墙地砖。为提供一种能够降低成本，且能保证产品质量的陶瓷墙地砖而研制。所述墙地砖的坯体是由下述百分比含量的原料制成的：煤矸石３０％－４０％，粉煤灰２％－８％，废玻丝１％－３％，绿豆岩５０％－５８％，白泥２％－６％。由于在陶瓷墙地砖的坯料中使用了煤矸石、粉煤灰、废玻丝，不仅可以节省资源，保护植被，美化环境，变废为宝，而且由于绿豆岩和白泥配比得当，所以生产的产品质量稳定，大幅降低生产成本。

wall and floor tiles

The invention discloses a ceramic wall and floor tile. In order to provide a kind of ceramic wall tile which can reduce the cost and guarantee the quality of products. The body of the tile is prepared from the following raw materials: the percentage of coal gangue in 30% - 40%, 2% - 8% fly ash, waste Bosi 1% - 3%, 50% - 58% mung bean Rock white mud, 2% - 6%. The ceramic tile material used in the coal gangue, fly ash, waste Bosi, not only can save resources, protect vegetation, beautify the environment, but also because of treasure, mung bean rock and white mud in the proper ratio, so the stable quality of products, reduce production cost.

【技术实现步骤摘要】

本专利技术涉及一种陶瓷墙地砖。技术背景现有的陶瓷墙地砖多以长石、风化长石、高温砂、低温砂、页岩、白泥、 黑泥等为主要原料生产白坯砖或红坯砖，这种作法，对环境、植被破坏严重， 而且浪费资源，为此国家有关政策倡导要有效利用资源、综合利用资源、尽可 能的废弃物再利用。
技术实现思路
本专利技术目的在于提供一种能够降低成本，且能保证产品质量的陶瓷墙地砖。 为达到上述目的，本专利技术陶瓷墙地砖的坯体是由下述百分比含量的原料制成的煤矸石30%—40%,粉煤灰2%—8%，废玻丝1%—3%，绿豆岩50 %—58%，白泥2%—6%。本专利技术在陶瓷墙地砖的坯料中使用了煤矸石、粉煤灰、废玻丝，不仅可以 节省资源，保护植被，美化环境，变废为宝，而且由于绿豆岩(钾土)和白泥 (粘土)配比得当，所以生产的产品质量稳定，大幅降低生产成本。具体实施方式本专利技术陶瓷墙地砖的坯用原料 煤矸石百分比含量30%—40%，最佳为35%。化学组成IL (烧失量)<8， Si02 (氧化硅)60—70， Fe203 (氧化铁)< 2， A1203 (氧化铝)17—23， MgO (氧化镁)&lt;0.5， Ca本文档来自技高网...

【技术保护点】
一种陶瓷墙地砖，其特征在于：所述墙地砖的坯体是由下述百分比含量的原料制成的：煤矸石３０％－４０％，粉煤灰２％－８％，废玻丝１％－３％，绿豆岩５０％－５８％，白泥２％－６％。