The invention relates to a biodegradable refractory ceramic fiber and a preparation method thereof. The technical scheme is: 18 ~ 25wt% or 28 ~ 33wt% talc dolomite, 15 ~ 40wt%, 30 ~ 50wt% wollastonite quartz sand, 0.5 industrial grade calcium chloride, 3wt% 0.5 ~ 3wt% 0.2 ~ fluorite, rare earth metal oxide 2wt% and 0 ~ 3wt% zircon sand the mill, plus 0.5 ~ 3wt% carboxymethyl cellulose or lignin calcium sulfonate as binder; then the mixture is pressed into a blank, drying and crushing; then the crushed material is placed in the resistance furnace or arc furnace heated to 1500 to 1900 DEG C, after melting or directly thrown silk or in 0.3 ~ 0.7MPa under the conditions of the the blown. The invention selects natural minerals as raw materials, low cost and simple process; the preparation of biodegradable refractory ceramic fiber with high mechanical strength, smooth surface, uniform fiber chemical composition, can long at 1000 to 1200 DEG C or higher temperature on human body, greatly reduce the harmful.
【技术实现步骤摘要】
本专利技术涉及。具体涉及一种采用天然矿物 原料所制备的生物可降解性耐火陶瓷纤维及其制备方法。
技术介绍
目前主要使用的传统的耐火陶瓷纤维多为硅酸铝系陶瓷纤维，含有相对较高的Al203和 较低的Si02，为偏碱性。传统的耐火陶瓷纤维在生产和使用中产生的大量粉尘吸入人体肺部后，在肺液中不能得到充分降解而在肺部沉积，对人体健康产生危害。按照欧盟规定，传统 的耐火陶瓷纤维均属于很可能致癌物，达不到环保的要求。目前己投入市场或公开的技术资料中，生物可降解性耐火陶瓷纤维多为钙镁硅系纤维， 由该系统派生出的另一类生物可降解性耐火陶瓷纤维是硅酸镁系统纤维，该类纤维的使用温度为126(TC或更高，与传统的硅酸铝系纤维相当，与钙镁硅系纤维相比，导热系数偏高。目 前的生物可降解性耐火陶瓷纤维仍存在一定的缺陷，如成本价格相对传统陶瓷纤维偏高、使 用温度不高、纤维机械强度低，以及高温使用后脆性增大等。
技术实现思路
本专利技术旨在克服上述技术缺陷，目的是提供一种成本较低、工艺简单的生物可降解性耐 火陶瓷纤维的制备方法；用该方法所制备的生物可降解性耐火陶瓷纤维机械强度高、表面光 滑、纤维化学组...
【技术保护点】
一种生物可降解性耐火陶瓷纤维的制备方法，其特征在于将１８～２５ｗｔ％的滑石粉或２８～３３ｗｔ％的白云石、１５～４０ｗｔ％的硅灰石、３０～５０ｗｔ％的石英砂、０．５～３ｗｔ％的工业级氯化钙、０．５～３ｗｔ％的萤石、０．２～２ｗｔ％的稀土金属氧化物和０～３ｗｔ％的锆英石砂细磨，外加０．５～３ｗｔ％的羧甲基纤维素或木质素磺酸钙为结合剂；再将上述混合料压制成坯、干燥和破碎，破碎后置于电阻炉或电弧炉中升温至１５００～１９００℃；熔融后或直接甩丝或在０．３～０．７ＭＰａ的条件下经喷吹成纤。
【技术特征摘要】
【专利技术属性】
技术研发人员：王玺堂，刘浩，张保国，王周福，
申请(专利权)人：武汉科技大学，
类型：发明
国别省市：83[中国|武汉]