The invention relates to an application of noctilucent powder in the manufacture of ceramic balls, ornaments, glazed tiles and accessories thereof, belonging to the technical field of building materials. The invention adopts luminous powder and frit mixed according to weight percentage, mixing ratio: 10 luminous powder - 50%, 50 - 90% of pigment frit; spray well mixed in a burning and spraying white glaze or ceramic pigment products, as the application of ceramic pigment surface treatment products. The invention has the advantages of simple preparation method, expand the application of luminous powder, using luminous powder products, absorb and store light in the daytime, night release source; its products not only appreciate the appearance of new, colorful, high artistic value, but also has the illumination function for miniature lamps can.
【技术实现步骤摘要】
本专利技术涉及一种夜光粉在制作陶瓷圆球、饰品、琉璃瓦及其配件中的 应用,属建筑材料
技术介绍
目前,市场上销售的陶瓷产品已有多种,基本能够满足需求。但产品 表面欠美观。迄今为止,未见与本专利技术相同的公开报道。
技术实现思路
本专利技术的目的在于提供一种夜光粉在制作陶瓷圆球、饰品、琉璃瓦及 其配件中的应用。本专利技术采用市场上销售的夜光粉与熔块按重量百分比混合,混合比例 为夜光粉10-50%、熔块50-90%;将混合好的原料作为表面处理颜料,喷 在经一次素烧并喷了白色底釉或陶瓷颜料的产品上,喷的厚度为 0.05-0. 5mm,随后放入常规锻烧炉内,锻烧3-10小时,当温度达到700-1100 "后得到陶瓷产品,自然冷却后取出。.本专利技术特别适宜在制备陶瓷圆球、饰品(如鸽子等)、琉璃瓦及其配件 中应用。本专利技术的优点在于制备方法简单、拓展了夜光粉的应用,使用了夜 光粉的产品,白天吸光和蓄光,夜晚自然释放光源;其产品不仅外观新颖、 色彩斑斓、艺术欣赏价值高,还兼有微型灯的照明功能。 具体实施例方式实施例l:(制备陶瓷圆球)本专利技术采用市场上销售的夜光粉与高铅低温熔块按重量百分比混合, 混合比例为夜光粉50%、高铅低温熔块50%;将混合好的颜料作为表面处 理的颜料,喷在经一次素烧并喷了白色底釉或陶瓷颜料的产品上,喷的厚度为0. 2mm,随后放入常规锻烧炉内,锻烧10小时,当温度达到IIO(TC后得 到陶瓷产品,自然冷却后取出。实施例2:(制备饰品如鹆子)基本同实施例1。不同之处为夜光粉40%、熔块60%;锻烧3小时,当温度达到70(TC后得到陶瓷产 ...
【技术保护点】
一种夜光粉在制作陶瓷圆球、饰品、琉璃瓦及其配件中的应用,其特征在于:采用夜光粉与熔块按重量百分比混合,混合比例为:夜光粉10-50%、熔块50-90%;将混合好的颜料喷在经一次素烧并喷了白色底釉或陶瓷颜料的产品上,作为陶瓷产品表面处理颜料的应用。
【技术特征摘要】
【专利技术属性】
技术研发人员:谢礼荣,刘俊优,
申请(专利权)人:谢礼荣,刘俊优,
类型:发明
国别省市:53[中国|云南]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。