The utility model relates to a crushed stone concrete porous brick, relating to a building material, in particular to a porous brick for industrial and civil buildings. It consists of the following material quality percentage: the combination of a 50 - 70%, 20 - 40% of the debris of fly ash, 3 - 10%, 2 - 5% lime cement, 0.5 - 2% of the admixture; the above materials are mixed and stirred with proper amount of water by a brick into the mechanism of multi hole brick need specifications. The present invention applies crushed stone as main material, reduces manufacturing cost, and ensures the strength and density of porous brick so as to meet industrial and civil standards. The invention has the advantages of simple production process and low cost of production material, can meet the relative standards of national architecture, porous brick strength, density level and drying shrinkage rate are in line with national requirements.
【技术实现步骤摘要】
本专利技术涉及一种建筑材料，具体涉及一种工业和民用建筑用多孔砖。
技术介绍
随着社会经济的发展、人们生活水平的提高，工业、民用建筑越 来越多，国家规定不再允许使用粘土烧砖，中国持续千年的粘土红砖 在作出巨大贡献后即将退出，由于粘土红砖需要耗费大量的粘土，烧 制红砖需要破坏大量的耕地。目前很多制砖企业都是采用了各种原材 料烧制多孔砖，目前应用比较多的是水泥混凝土多孔砖、粉煤灰多孔 砖，水泥混凝土多孔砖是目前应用比较多的，但是水泥混凝土多孔砖 木身制造成本较高；粉煤灰多孔砖由于粉煤灰木身的强度不够， 一直 没有得到广泛应用，而且其工艺复杂，应用较为困难。
技术实现思路
本专利技术的目的是提供一种碎石屑混凝土多孔砖，它具有生产工艺 简单、生产材料成本低的优点，能够符合国家建筑相关的各项标准， 多孔砖的强度等级、密度等级、干燥收縮率等均符合国家要求。为了 解决
技术介绍
所存在的问题，本专利技术是釆用以下技术方案它由以下 质量百分比的材料组合而成50-70%的碎石屑、20_40%的粉煤灰、 3-10%的生石灰、2-5%的水泥、0.5-296的外加剂；将上述材料混合后 加入适量的水搅拌，利用制砖机制成所需要规格的多孔砖。本专利技术用 碎石屑作为主要材料，降低了制造成本，也保证了多孔砖的强度和密 度，使之达到工业和民用的标准。本专利技术具有生产工艺简单、生产材料成本低的优点，能够符合国家建筑相关的各项标准，多孔砖的强度等级、密度等级、干燥收縮率等均符合国家要求。具体实施例方式本具体实施方式采用以下技术方案它由以下质量百分比的材料 组合而成60%的碎石屑、30%的粉煤灰、5...
【技术保护点】
一种碎石屑混凝土多孔砖，其特征在于它由以下质量百分比的材料组合而成：５０－７０％的碎石屑、２０－４０％的粉煤灰、３－１０％的生石灰、２－５％的水泥、０．５－２％的外加剂。