The invention relates to a method for manufacturing a glass mosaic, which is characterized in that the waste glass is used as the main raw material, a new molding adhesive (glue solution), an inorganic colorant and a set of corresponding sintering techniques are used. The forming pressure is 150-450 kg / cm + [2], and the minimum firing temperature is 650~800 DEG C, which is sintered in a continuous tunnel kiln. Defoaming agent is not needed; because of good properties of binder and low dosage, it can be quickly burnt. Resulting in a variety of color products, no bubbles, visual sense of strong, fine texture.
【技术实现步骤摘要】
本专利技术所涉及的是一种建材制品的制造方法。玻璃马塞克主要应用于建筑物的内外墙装饰,它具有良好的使用性能与物理力学指标,有广泛的应用前景。建筑物的内外墙用玻璃马塞克饰面后,使用寿命长,不需要复涂或翻修,因而大大减少了维修费用。已知生产玻璃马塞克的粉末烧结方法均采用玻璃粉料压制并经烧结而成,所不同的是日本(特许开昭55-11620)采用粉料玻璃中掺加碱金属硅酸盐水溶液作粉料成型粘结剂并需加入3%(重量百分数)氧化锌和1.5%(重量百分数)缩合磷酸盐作抑泡剂以防止粘结剂在烧结时发泡。法国(专利Fr220789)则介绍玻璃粉料需用水与有机粘结剂拌混,其重量百分比分别为玻璃粉占67%,水占30%,粘结剂占3%。在苏联,制造玻璃马塞克采用在玻璃粉料中掺加5%(重量百分数)的石腊作为成型粘结剂。采用上述数种粘结剂导致产品成本增加,影响产品质量及污染环境。本专利技术的目的在于提供一种制造玻璃马塞克的新方法。采用废玻璃作主要原料,改用新的成型粘结剂,无机着色剂及一整套相应的制备流程达到降低成本,提高质量,无环境污染,工艺简单的目的。本专利技术所述制造玻璃马赛克的方法主要包括以下内容(1)采用废玻璃(平板、瓶罐、棒、管等玻璃废品)为主要原料经过粉碎后过40-100目/吋2的筛子。粉碎玻璃可用轮碾机积球磨机,粉末玻璃用振动筛过筛。()(2)按需要加入一定量的无机颜料着色剂,并混合均匀,混色可在拌料机或球磨机内进行。(3)用印染脱水溶液作粘结剂,浓度为1-5%(重量百分数),粘结剂用量约为玻璃粉重量的0.1~0.3%,视制品大小粘结剂用量可调节,可用拌料机将粘结剂与玻璃粉料拌混均 ...
【技术保护点】
一种用废玻璃粉料压制成型并烧结的生产玻璃马赛克的方法,其特征在于:a.采用无机颜料着色剂将马赛克着色,所用着色剂是:钛白粉、铬绿铁黑、铁红、黄色素、色素、黑色素;浓度范围为0.05-2%(重量百分数);b.采用印染胶水溶液作玻璃粉料 成型粘结剂;c.粉料需在150-450公斤/厘米↑〔2〕的压力下加压成型;d.成型的坯料需在650-800℃下进行高温烧结;e.需控制升、降温速率。
【技术特征摘要】
1.一种用废玻璃粉料压制成型并烧结的生产玻璃马赛克的方法,其特征在于a.采用无机颜料着色剂将马赛克着色,所用着色剂是钛白粉、铬绿铁黑、铁红、黄色素、色素、黑色素;浓度范围为0.05-2%(重量百分数);b.采用印染胶水溶液作玻璃粉料成型粘结剂;c.粉料需在150-450公斤/厘米2的压力下加压成型;d.成型的坯料需在6...
【专利技术属性】
技术研发人员:方之耀,陈学娴,朱亚娟,沈崇德,陈铁姗,