A method for making rainbow glass transfer method, which is characterized in that the grating fabrication metal reflective layer is transferred to the glass surface, eliminating the vacuum coating process, so the process is simple, less investment in equipment, the protective layer of selected material can not only play a protective function, and has the ability to support the stability of grating structure the product is low cost, good quality, can withstand all kinds of bad environment, the rainbow glass production difficulty is greatly reduced, used more widely.
【技术实现步骤摘要】
本专利技术涉及一种装饰用彩虹玻璃的制作工艺,特别涉及采用较少的工序获得高质量的彩虹玻璃的制作工艺。彩虹玻璃也称光栅玻璃或镭射玻璃,现有的制作方法一般是在玻璃表面涂一层透明树脂胶,然后用光栅模具在树脂层上压印上光栅,再送镀膜机镀反射膜,或者是在树脂层上粘贴一层带有光栅的塑料膜,这些方法难免具有工序复杂,设备投资大,光栅结构在复制过程损失较大,导致产品变彩效果差,亮度低等弱点,同时这些方法生产的产品在安装使用时还会出现不便于切割和粘贴的麻烦。本专利技术的目的在于采用一种新工艺,以较为简便的制作方法,较少的设备投资,获得一种内在质量优良,外观好,便于使用安装的彩虹玻璃,使这一产品的生产难度降低,使用范围更加广泛。本专利技术的目的是这样实现的,先将透明环氧树脂加入固化剂,偶联剂,促进剂,调配成一种能与玻璃表面和金属表面形成较大粘结力的结构胶,将这种结构胶涂于清洁过的玻璃表面,然后将压好光栅并镀好金属反光层的塑料膜片紧贴于涂有结构胶的一侧,待结构胶固化后不仅能够无损失地复制出膜片上的光栅结构,同时由于结构胶与玻璃表面和金属反光层之间形成的拉力远大于塑料膜与金属反光层之间的拉力,因此可将塑料膜揭去,这时带有光栅结构的金属反光层便完好无损地被转移到了结构胶上,最后在金属面上涂制一层高硬度保护层,这层保护层不仅可以起到保护光栅结构和反光层的作用,同时可在与金属反光层接触的一侧再次复制出一层光栅层,形成双光栅夹一层反光层的特殊结构,使本方法制作的彩虹玻璃的光栅结构高度稳定,寿命长,能耐受各种不良环境。上述工艺方法中,结构胶的化学特点决定了它与玻璃表面和金属反光层表面形 ...
【技术保护点】
转移法制作彩虹玻璃的方法,其工序为:(1)用乙醇和丙酮分别对玻璃表面进行清洁,(2)将调配好的透明结构胶均匀地涂布于玻璃表面,其厚度小于0. 1毫米,(3)将压印好光栅并镀好金属反光层的塑料膜片或镭射电化铝膜片紧贴于胶面,应使膜片 的金属面在胶面一侧,并排尽气泡,(4)将完成上述工序的产品在20~40摄氏度环境中固化24~48小时,(5)将塑料膜揭去,玻璃表面留下光栅结构和金属反光层,(6)在金属面上涂制保护层。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。