玻璃介质激光工作物质表面微裂纹溶蚀钝化处理方法技术

玻璃介质激光工作物质表面微裂纹溶蚀钝化处理方法，涉及激光应用技术，采用质量浓度为３５～４５％的氢氟酸（ＨＦ）溶液，将激光工作物质全部浸没在溶液内，控制溶蚀时间在５～８Ｈ，使得激光工作物质表面部分被溶蚀钝化，本发明专利技术大大提高了激光工作物质热开裂时的应力极限，确保了冷却条件下，激光工作物质的重复率运转的安全性，操作方法简单、处理成本低廉、处理后的成效显著。

Method for dissolving and passivating micro cracks on laser working substance of glass medium

The surface of the glass medium laser material micro crack corrosion passivation method, relates to the application of laser technology, the mass concentration is 35 ~ 45% of hydrofluoric acid (HF) solution, the laser material are immersed in a solution, dissolution time control in 5 ~ 8H, the laser material surface by dissolution passivation, the invention greatly improves the the ultimate stress of hot cracking of the laser work material, to ensure the safety of the cooling conditions, repetition rate of laser material operation, simple operation, low cost, after the remarkable results.

【技术实现步骤摘要】

本专利技术涉及激光应用技术，特指一种针对玻璃介质激光工作物质表面微裂纹的处理方法，以提高玻璃介质激光工作物质实际应用时的热应力损伤阈值。
技术介绍
在国内首台重复率千兆瓦钕玻璃激光冲击加工系统中，一个重要的特点就是钕玻璃激光工作物质重复率工作带来的问题。即由于重复率(0.5Hz)光泵，激光工作介质内的热积累来不及被恒温循环冷却液带走，温度逐渐上升，从而在横截面上形成了中心温度高、边缘温度低这样的温度梯度分布。因此引起材料热膨胀的不均匀性，导致在激光工作物质表面形成张应力，中心形成压应力。对于一定体积的激光工作物质，随着平均光泵功率的提高，激光工作物质横截面上的温度梯度同样随之提高，进而导致激光工作物质表面的张应力及中心的压应力增大。毛化处理的激光工作物质表面往往由于微裂纹等缺陷使得其表面损伤阈值要低于体损伤阈值，而激光介质表面在压应力下的表面损伤阈值至少是在张应力下的表面损伤阈值的5倍以上，当张应力超过材料的抗张极限时，就会导致激光工作物质开裂。因此如何有效消除激光工作物质表面的微裂纹，是提高激光工作物质热应力损伤阈值的关键。高功率固体激光系统为了消除寄生振荡，通常是把棒状激光工本文档来自技高网...

【技术保护点】
玻璃介质激光工作物质表面微裂纹溶蚀钝化处理方法，其特征在于：采用质量浓度为３５～４５％的氢氟酸（ＨＦ）溶液，将玻璃介质激光工作物质全部浸没在溶液内，控制溶蚀时间在５～８Ｈ，使得激光工作物质表面部分被溶蚀钝化。

【技术特征摘要】

【专利技术属性】
技术研发人员：李国杰，张永康，李应红，杨兴华，冯爱新，周建忠，马壮，
申请(专利权)人：江苏大学，
类型：发明
国别省市：32[中国|江苏]