The invention discloses a self focusing lens glass and its production method and use of the ion exchange of the glass furnace, according to weight ratio, including: 3045% SiO: 2, 06% K: 2 O, 512% Na: 2 O, 612% ZnO, 3246% Tl: 2 O, 2-10% B: 2 O: 3, 05% Nb: 2 O: 5. The average oxygen number of oxygen polyhedron is Y 3. SiO: 2 and B: 2 O: 3 of the content and in accordance with the molar percentage of 5059%. B: 2 O: 3. The content of SiO or down 2 and B down 2 O down 3 and the content in accordance with the molar percentage of 5-8%. The method of self focusing lens of glass production, the method comprises the following steps: the order of glass batch, the smelting, the casting, the annealing, the optical cold processing, thrown into a cylindrical rod, the grinding, wire drawing, and ion exchange to optical cold processing, the coating. Three \K\ dividing thermocouples are arranged in the furnace, and the furnace is provided with an acid resistant stainless steel inner liner. The furnace wall is provided with three thermocouples and an armored thermocouple.
【技术实现步骤摘要】
本专利技术涉及光学玻璃，尤其是涉及一种自聚焦透镜玻璃及其生产方法和使用的离子交换炉。
技术介绍
径向变折射率透镜即自聚焦透镜，之所以受到人们的特别关注，主要是因为它的直径小、焦距短、数值孔径大，而且具有对光束聚焦、对物体成像的能力。因此，它是一种很重要的微小光学基础元件，在光纤通信、光纤传感、光信息处理和其他许多领域中有重要应用。然而，实际光学系统成像与理想光学系统成像之间存在着偏差，这种光学系统成像的偏差，称为系统的像差。用于内窥的自聚焦透镜成像后，导致图像清楚度不均匀，像差主要是畸变和球差。目前改善自聚焦透镜像差的方法主要是二次离子交换法和热处理方法，但这都是在第一次离子交换后再进一步处理，所以增加了程序使工艺复杂化。由于不是从根本上即玻璃配方上进行改进，折射率分布曲线会出现折点，不是平滑连续，尤其是热处理法，虽然它可以对边缘区的较陡峭的折射率变化予以修正，但中心折射率仍会下降，而且对于不同的配方未必都适用。由于Tl2O的电极化率大，易于离子交换，通常选用Tl+用在自聚焦透镜玻璃中，为了提高玻璃的折射率，以增加自聚焦透镜的数值孔径，需要加入玻璃中Tl+的量很...
【技术保护点】
一种自聚焦透镜玻璃，其特征在于：该玻璃按重量配比，包括：３０－４５％的ＳｉＯ↓［２］，０－６％的Ｋ↓［２］Ｏ，５－１２％的Ｎａ↓［２］Ｏ，６－１２％的ＺｎＯ，３２－４６％的Ｔｌ↓［２］Ｏ，２－１０％的Ｂ↓［２］Ｏ↓［３］，０－５％的Ｎｂ↓［２］Ｏ↓［５］。
【技术特征摘要】
【专利技术属性】
技术研发人员：蔡春平，高秀敏，徐秋霜，强西林，
申请(专利权)人：徐秋霜，
类型：发明
国别省市：94[中国|深圳]