The aim of the invention is to use intermediate film insulation interlayer film for laminated glass modification method, thermal insulation interlayer film for laminated glass, and laminated glass which even in the use of insulating particles covered by an inert substance under the condition can also be obtained can exert excellent optical performance of the insulation laminated glass provides. Insulation interlayer film for laminated glass modification method, thermal insulation interlayer film for laminated glass and laminated glass features is covered by an inert substance containing insulating particles, matrix resin and liquid intermediate film for laminated glass insulation plastic agent increased by irradiation with high energy radiation has more than 3.0eV of energy of electromagnetic wave the enhanced visible light transmittance wavelength of 380 to 780nm, while reducing the near infrared transmittance wavelength of 780 to 2100nm.
【技术实现步骤摘要】
【国外来华专利技术】
本专利技术涉及一种即使在使用由惰性物质覆盖的隔热性微粒的情况下也能得到可以发挥出色的光学性能的隔热夹层玻璃用中间膜的、隔热夹层玻璃用中间膜、以及夹层玻璃。
技术介绍
就夹层玻璃而言，即使受到外部冲击发生破损也很少发生玻璃破片的飞散，而比较安全，所以被广泛用作汽车等车辆、飞机、建筑物等的窗玻璃等。作为上述夹层玻璃，可以举出在至少一对玻璃之间例如存在由被增塑剂增塑的聚乙烯醇缩丁醛树脂等聚乙烯醇缩醛树脂构成的夹层玻璃用中间膜、并使其一体化而成的夹层玻璃等。但是，使用这样的夹层玻璃用中间膜的夹层玻璃，尽管安全性出色，但隔热性差。在光线中具有比可见光长且为780nm以上的波长的紫外线，尽管与紫外线相比能量小约为10％左右，但热作用大，一旦被物质吸收而作为热被释放出，会引起温度上升，所以通常称为热射线。因而，只要能够遮挡例如从汽车的挡风玻璃或侧窗玻璃入射的光线中热作用大的红外线(热射线)，其隔热性就增高，可以抑制汽车内部的温度上升。作为近年来的趋势，汽车等中的玻璃开口部分面积增大、提高夹层玻璃的隔热性、向玻璃开口部分赋予热射线切断功能的必要性增大。与此相对，在专利文献1中...
【技术保护点】
一种隔热夹层玻璃用中间膜的改性方法，其特征在于，对含有由惰性物质覆盖的隔热性微粒、基质树脂以及液态增塑剂的隔热夹层玻璃用中间膜，通过照射含具有３．０ｅＶ以上的能量的电磁波的高能量射线，提高波长３８０～７８０ｎｍ的可见光透射率，同时降低波长７８０～２１００ｎｍ的近红外线透射率。
【技术特征摘要】
【国外来华专利技术】...
【专利技术属性】
技术研发人员：八田文吾，深谷重一，
申请(专利权)人：积水化学工业株式会社，
类型：发明
国别省市：JP[日本]