本发明专利技术是一种以ＭＣＶＤ工艺制造高带宽渐变型多模光纤的方法。采用一次近似法实现光纤予制棒折射率的精确控制，烧缩时补芯与腐蚀相结合获得了极窄的中心折射率凹陷。解决了常规的０次近似法和经验修正法中折射率分布指数α的分散性及重复性差的问题。所制造的多模光纤折射率控制精度达５×１０＋［－５］，１．３μｍ处平均带宽＞１７００ＭＨ－［Ｚ］.Ｋｍ最高达５ＧＨ－［Ｚ］.Ｋｍ，传输损耗０．５～１．０ｄＢ／Ｋｍ，可用于三、四次群光纤通信领域。（*该技术在2008年保护过期，可自由使用*）

Manufacturing method of high bandwidth gradual change multimode optical fiber

The invention relates to a method for manufacturing a high bandwidth gradual change multimode optical fiber by using MCVD process. The first approximation method to achieve precise control of the refractive index of the optical fiber rods, burning and corrosion combination helps make up the core to get the center narrow depression rate index. The dispersion and repeatability of the index of refractive index distribution in the conventional 0 approximation method and the empirical correction method are solved. Multimode fiber made by the refraction rate control accuracy of 5 * 10 + / - 5, 1.3 m, the average bandwidth 1700MH Z.Km up 5GH Z.Km, the transmission loss of 0.5 ~ 1.0dB / Km, can be used for three or four times in the field of optical fiber communication group.

【技术实现步骤摘要】

【技术保护点】
一种高带宽渐变型多模光纤的制造方法，采用ＭＣＶＤ工艺制备光纤予制棒（该工艺包括在石英包皮管内沉积组分为Ｆ－Ｐ↓〔２〕Ｏ↓〔３〕－ＳｉＯ↓〔２〕三元系的包层，沉积组分为ＧｅＯ↓〔２〕－Ｐ↓〔２〕Ｏ↓〔５〕－ＳｉＯ↓〔２〕三元系的芯层时只改变主掺杂剂ＧｅＣｌ↓〔４〕的流量，将沉积好的石英管烧缩成实芯棒），然后将所得予制棒拉成光纤，其特征是采用一次近似法控制ＧｅＣｌ↓〔４〕的载气流量Ｆ↓〔ｉ〕相对于喷灯移动次数ｉ的变化，一次近似的计算公式如下：Ｆ↓〔ｉ〕＝Ｆｏ〔１－（１－ｉ／Ｎ ）↑〔ａ／２〕〕.｛１＋β〔１－（１－ｉ／Ｎ）↑〔ａ／２〕｝式中Ｆ↓〔１〕为第ｉ层的ＧｅＣｌ↓〔４〕载气流量（ｍｌ／...

【技术特征摘要】

【专利技术属性】
技术研发人员：梁建明，王旭华，
申请(专利权)人：杭州无线电材料厂，
类型：发明
国别省市：33[中国|浙江]