The invention discloses a method for manufacturing a heat-resistant fireproof super toughened safety glass plate, which can be used to produce a heat-resistant fireproof super toughened safety glass plate by using an ordinary tempering furnace device. Heat resistant fireproof super toughened glass plate in case of fire at 1000 degrees Celsius can adhere to 90 minutes without cracking. Its impact strength is 1 times higher than that of ordinary tempered glass plate, and the amount of broken particles in 5cm * 5cm area is more than 400. The invention is realized through the production technique scheme: the use of ordinary steel furnace, the glass plate of different thickness on the lower surface of the rapid quench blowing, blowing pressure increase 4 ~ 20 times, reducing the internal tensile stress layer and the thickness of the glass sheet through a substantial increase in glass surface compressive stress the thickness of the layer, can produce heat resistant fireproof super toughened glass plate. \ue5cf
【技术实现步骤摘要】
本专利技术是关于耐热防火超强钢化安全玻璃板的生产制造方法，更具体的说，本专利技术是利用普通的钢化炉，使用新的工艺技术生产制造耐热防火超强钢化安全玻璃板。
技术介绍
普通的钢化安全玻璃板是将玻璃板在钢化炉中加热至接近软化点后再迅速进行吹风冷却，在玻璃板的上下表面制造出压应力层，从而生产出安全玻璃。不同厚度的玻璃板在加工时，采用不同的风压对玻璃板的上下表面进行急速吹风急冷。生产的普通钢化安全玻璃板上下表面产生应力层的厚度是玻璃板厚度的六分之一左右。玻璃板破碎时，整块玻璃板全部碎成蜂窝状钝角小颗粒，5cm×5cm面积内的破碎颗粒数量在40～50粒左右。普通钢化安全玻璃板的机械强度是普通平板玻璃的3倍左右。普通钢化安全玻璃板不具有防火功能，在受到火焰冲击后的6～8分钟左右会炸裂。
技术实现思路
本专利技术是利用普通的钢化炉，在对不同厚度的玻璃板上下表面进行急速吹风急冷时，加大吹风的压力，其风压增加的量是过去生产不同厚度普通钢化安全玻璃板压力的4～20倍左右。利用新的生产工艺技术能大幅度提高玻璃板上下表面压应力层的厚度，降低玻璃板内部张应力层的厚度。采用本专利技术新的工艺技...
【技术保护点】
一种耐热防火超强钢化安全玻璃的制造方法其特征在于，它使用普通的钢化炉设备生产耐热防火超强钢化安全玻璃。