The present invention provides a method for implementation of oxygen enriched combustion and a glass furnace in air combustion in glass furnace, the method comprises the following steps: using a combustion fan into the hot air from the melting pool of the crown; the oxygen pass into the air outlet of the air blower, the oxygen and air mixed combustion air to become; the combustion and combustion air into regenerator. The method and the glass tank furnace of the invention can effectively save energy and reduce consumption and stabilize the pool furnace process, and is one of the most direct methods for enterprises to reduce production costs. At the same time, the oxygen content of each small furnace can be effectively realized, and the effective control of the atmosphere can be achieved, and favorable conditions for stabilizing and reducing the bad glass are provided.
【技术实现步骤摘要】
本专利技术属于玻璃熔炼领域，特别涉及到一种在普通空气助燃玻璃池炉蓄热室上，直接实施富氧燃烧的改造方法。
技术介绍
据统计，中国现有工业窑炉约80万台，年消耗能源1.9亿吨标准煤，约占全国能源消费总量的五分之一，节能潜力很大。燃烧是由于燃料分子和氧气分子之间发生高能碰撞而引起的。在常规的空气燃烧系统中，这种作用受到氮气分子的严重阻碍，一方面，氮气在高温下与氧气反应，并吸收热量；另一方面，减少了氧分子与燃料分子之间的碰撞机会。普通空气中的氧只占21％，含量最多的是氮，占79％。因此在燃烧过程中，近80％的不助燃氮气吸收了大量热量，在废气中排掉，造成热量的无谓消耗。同时在高温下生成氮氧化物，污染大气。在目前，国内大多数玻璃窑炉采用蓄热式横火焰窑炉，它是利用熔化池两侧的蓄热室内的格子体吸收燃烧废气余热，同时将助燃空气预热，这种蓄热式空气预热燃烧技术能够大幅降低燃料用量。图1、图2分别为玻璃池炉的平面图、立体图。在图1和图2中，在熔化池1的两侧分别是蓄热室2。但是当池炉进入后期，蓄热室部分格子体坍塌，蓄热能力下降，积渣严重，导致池炉燃烧状况变差，助燃空气进入熔化池前不能...
【技术保护点】
一种在空气助燃玻璃池炉中实施富氧燃烧的方法，该方法包括步骤：利用助燃风机从熔化池的碹顶引入热风；在助燃风机的出风口处通入氧气，使氧气和热风混合成为助燃风；将助燃风送入蓄热室进行助燃。
【技术特征摘要】
【专利技术属性】
技术研发人员：李留恩，贾伟，苍利民，韩广军，张军，胡喜宾，谷凡，
申请(专利权)人：河南安彩高科股份有限公司，
类型：发明
国别省市：41[中国|河南]