A waterproof inner wall decoration coating, which consists of the following parts by weight: 8-14 portions of raw material made of thermosetting plastics, oaklet tree sawdust 4-6, 2-4 diatomite, Kim Pachystachys sawdust powder 10-16, melamine resin 12-23, silicate fiber cotton 5-8, magnesium hydroxide 7-12, ethanol 15-25, hydrochloric acid solution 2-5, acetyl acetone 4-7, 1-2 latex powder, inorganic thickener 6-14, polyether polyol 25-35, phenolic resin 8-13, alumina 3-5, stabilizer 1-3, dispersant 1.2-2.5, hydroxyethyl cellulose 2-5. The invention has the advantages of stability, durability, environmental protection, good abrasion resistance, high toughness, good resistance to abrasion and high toughness, and is not easy to fall off and crack.
【技术实现步骤摘要】
本专利技术涉及一种耐水性内墙装饰涂层。
技术介绍
我国建筑装饰行业近年来发展很快,建筑装饰为人们提供了一个使用便捷、舒适、安全且具有完美艺术性的空间环境。建筑改善了居住、办公、娱乐条件,提高了生活、生产环境质量,满足了人的物质与精神需要,有利于身心健康。“墙面”装饰逐步成为家居装修的重头戏,各类饰面资料也是层出不穷,质感涂料、艺术涂料、手绘涂料确实各有所长。如今,人们对装饰材料的要求越来越高,尤其对内墙装饰涂层材料的要求更高,其直接关系到人们的舒适性和健康。但目前市场上的涂层材料还存在许多缺点,防潮、抗菌性不佳,稳定性和耐水性还有待于进一步改善。
技术实现思路
针对现有技术的不足,本专利技术要解决的问题是,提供一种耐水性内墙装饰涂层,具有稳定性、耐久性、环保性,耐磨、高韧性极佳,不易脱落和龟裂,使用寿命长。为解决上述技术问题,本专利技术的技术方案是,一种耐水性内墙装饰涂层,其由以下重量份数的原料制成:热固性塑料8-14份,枹树木屑4-6份,硅藻土2-4份,金苞花木屑粉末10-16份,密胺树脂12-23份,硅酸纤维棉5-8份,氢氧化镁7-12份,无水乙醇15-25份,盐酸溶液2-5份,乙酰丙酮4-7份,乳胶粉1-2份,无机增稠剂6-14份,聚醚多元醇25-35份,酚醛树脂8-13份,氧化铝3-5份,稳定剂1-3份,分散剂1.2-2.5份,羟乙基纤维素2-5份。优化的,一种耐水性内墙装饰涂层,其由以下重量份数的原料制成:热固性塑料11份,枹树木屑5份,硅藻土3份,金苞花木屑粉末13份,密胺树 ...
【技术保护点】
一种耐水性内墙装饰涂层,其特征在于:其由以下重量份数的原料制成:热固性塑料8‑14份,枹树木屑4‑6份,硅藻土2‑4份,金苞花木屑粉末10‑16份,密胺树脂12‑23份,硅酸纤维棉5‑8份,氢氧化镁7‑12份,无水乙醇15‑25份,盐酸溶液2‑5份,乙酰丙酮4‑7份,乳胶粉1‑2份,无机增稠剂6‑14份,聚醚多元醇25‑35份,酚醛树脂8‑13份,氧化铝3‑5份,稳定剂1‑3份,分散剂1.2‑2.5份,羟乙基纤维素2‑5份。
【技术特征摘要】
1.一种耐水性内墙装饰涂层,其特征在于:其由以下重量份数的原料制成:
热固性塑料8-14份,枹树木屑4-6份,硅藻土2-4份,金苞花木屑粉末10-16份,密胺树脂12-23份,硅酸纤维棉5-8份,氢氧化镁7-12份,无水乙醇15-25份,盐酸溶液2-5份,乙酰丙酮4-7份,乳胶粉1-2份,无机增稠剂6-14份,聚醚多元醇25-35份,酚醛树脂8-13份,氧化铝3-5份,稳定剂1-3份,分散剂1.2-2.5份,羟乙基纤维...