The invention relates to a method for flame retardant rubber products, the flame retardant rubber comprises the following components in part by weight: 140 rubber 170 copies, 14 copies, 10 black clay 6 9, calcium carbonate 10 16 copies, 8 copies, 3 zinc borate Zinc Oxide 5 7 copies, 7 aromatic oil 9 phthalate two formic acid and two butyl 1 4, two ethyl two zinc thiocarbamate 2 4, 2 3 thiol imidazoline 5, flame retardant 1 2 copies, 2 copies and 1 accelerator 1 plasticizer 2. The present invention by the flame retardant rubber was prepared by the preparation of components, simple preparation process, good flame retardant performance, and obtained by the invention of flame retardant rubber crafts is not easy to be burning in the fire, good quality, good performance, long service life.
【技术实现步骤摘要】
本专利技术涉及一种橡胶,具体说是一种用于工艺品的阻燃橡胶。
技术介绍
橡胶工艺品是以橡胶为主要原料,通过模具浇注成型,制成各种造型美观形象逼真的人物、动物、昆鸟、山水等,并可制成各种仿真效果,如:仿铜、仿金、仿银、仿水晶、仿玛瑙、仿大理石、仿汉白玉、仿红木等橡胶工艺品;但是现有技术中用于工艺品的橡胶不具备阻燃功能,导致工艺品在火灾中容易被烧坏,使用寿命短。
技术实现思路
针对上述技术问题,本专利技术提供一种用于工艺品的阻燃橡胶,制备成分少,制备工艺简单,阻燃性能好,通过本专利技术阻燃橡胶制备得到的工艺品在火中不易被燃烧,质量好,性能佳,寿命长。本专利技术所要解决的技术问题采用以下技术方案来实现:一种用于工艺品的阻燃橡胶,该阻燃橡胶由以下重量份的组分组成:橡胶140-170份、炭黑10-14份、陶土6-9份、碳酸钙10-16份、硼酸锌3-8份、氧化锌5-7份、芳烃油7-9份、邻苯二甲酸二丁酯1-4份、二乙基二硫代氨基甲酸锌2-4份、2-硫醇基咪唑啉3-5份、阻燃剂1-2份、促进剂1-2份和增塑剂1-2份。一种用于工艺品的阻燃橡胶,该阻燃橡胶由以下最佳重量份的组分组成:橡胶155份、炭黑12份、陶土7份、碳酸钙13份、硼酸锌6份、氧化锌6份、芳烃油8份、邻苯二甲酸二丁酯2份、二乙基二硫代氨基甲酸锌3份、2-硫醇基咪唑啉4份、阻燃剂1份、促进剂2份和增塑剂2份。作为本专利技术的一种优选技术方案,所述的橡胶为丁基橡胶、过氧氟橡胶和天然橡胶中的任意两种。本专利技术的有益效果是:相比现有技术,通过上述方式制备得到的阻燃橡胶,制备成分少,制备工艺简单,阻燃性能好,且通过本 ...
【技术保护点】
一种用于工艺品的阻燃橡胶,其特征在于:该阻燃橡胶由以下重量份的组分组成:橡胶140‑170份、炭黑10‑14份、陶土6‑9份、碳酸钙10‑16份、硼酸锌3‑8份、氧化锌5‑7份、芳烃油7‑9份、邻苯二甲酸二丁酯1‑4份、二乙基二硫代氨基甲酸锌2‑4份、2‑硫醇基咪唑啉3‑5份、阻燃剂1‑2份、促进剂1‑2份和增塑剂1‑2份。
【技术特征摘要】
1.一种用于工艺品的阻燃橡胶,其特征在于:该阻燃橡胶由以下重量份的组分组成:橡胶140-170份、炭黑10-14份、陶土6-9份、碳酸钙10-16份、硼酸锌3-8份、氧化锌5-7份、芳烃油7-9份、邻苯二甲酸二丁酯1-4份、二乙基二硫代氨基甲酸锌2-4份、2-硫醇基咪唑啉3-5份、阻燃剂1-2份、促进剂1-2份和增塑剂1-2份。2.根据权利要求1所述的一种用于工艺品的阻...
【专利技术属性】
技术研发人员:叶邦生,
申请(专利权)人:安徽省恒益工艺品有限公司,
类型:发明
国别省市:安徽;34