The invention discloses an anti graffiti paint, which is characterized by the following components according to a certain weight proportion: silicone modified acrylic resin 30 80; propylene glycol methyl ether 30 100; 1 dispersing agent 3; defoaming agent 1 8; ageings 2 3; leveling agent 1 7; 1 wetting agent 3. The present invention by methyl methacrylate, butyl acrylate, acrylonitrile and vinyl trimethoxysilane four monomers polymerized silicone modified acrylic resin, acrylic resin as preparation containing hydroxyl groups, in the film surface orientation and polymer structure and functional groups on the surface of coating in phase with hydrophobic crosslinking oleophobic properties obviously, and reduce dust, improve film cleaning, and the price is more economical. The invention has the advantages of obvious effect of preventing coating and hydrophobic, good stability of the coating, and can replace the organic fluorine modified coating with poor adaptability.
【技术实现步骤摘要】
本专利技术涉及涂料领域，具体涉及一种防涂鸦漆料。
技术介绍
近年来，空气质量越来越差，空气中颗粒及粉尘量越来越多，导致墙壁更易脏，清洗间隔时间也相应缩短，这使清洗对涂膜的破坏问题更加明显。市面上现有的易清洗的防涂鸦涂料，大多采用有机氟对涂料进行改性，但一般而言，有机氟改性涂料由于相对稳定性差，容易分解，防破坏性差，不适合同于户外环境，特别是一些恶劣的环境，有机氟改性涂料作为防涂鸦涂料更显得无能为力。
技术实现思路
针对现有技术的不足，本专利技术提供一种可适用于户外恶劣环境的防涂鸦涂料：一种防涂鸦漆料，其特征在于，由以下组份按照一定重量份配制而成：有机硅改性丙烯酸树脂 30-80份丙二醇甲醚 30-100份分散剂 1-3份消泡剂 1-8份防老化剂 2-3份流平剂 1-7份润湿剂 1-3份。作为优选的技术方案之一，其特征在于，所述的有机硅改性丙烯酸树脂由甲基丙烯酸甲酯、丙烯酸丁酯、丙烯腈及羟基乙烯基三甲氧基硅烷聚合而成。作为优选的技术方案之一，其特征在于，所述的防老化剂为酚类抗氧剂。作为优选的技术方案之一，其特征在于，所述的润湿剂为2-乙基己醇。本专利技术的有益效果是：本专利技术通过甲基丙烯酸甲酯、丙烯酸丁酯、丙烯腈及羟基乙烯基三甲氧基硅烷四种单体聚合而成的有机硅改性丙烯酸树脂，由于制备的丙烯酸树脂含有羟基官能团，能在涂膜表面定向排布并与涂料中的聚合物结构表面官能团相...
【技术保护点】
一种防涂鸦漆料，其特征在于，由以下组份按照一定重量份配制而成：有机硅改性丙烯酸树脂 30‑80份丙二醇甲醚 30‑100份分散剂 1‑3份消泡剂 1‑8份防老化剂 2‑3份流平剂 1‑7份润湿剂 1‑3份。
【技术特征摘要】
1.一种防涂鸦漆料，其特征在于，由以下组份按照一定重量份配制而成：有机硅改性丙烯酸树脂 30-80份丙二醇甲醚 30-100份分散剂 1-3份消泡剂 1-8份防老化剂 2-3份流平剂 1-...