一种轻质高强度墙体砖及其制备方法技术

本发明专利技术公开了一种轻质高强度墙体砖，制备时采用的原料重量份数为：硅沙170‑190份，水泥80‑90份，石灰35‑45份，磷石膏17‑24份，煤灰25‑35份，水320‑350份，铝粉0.3‑0.5份，云母粉25‑30份。发明专利技术的发泡方法为无机发泡，相比有机发泡具有更好的耐腐蚀和防火性能，并且更加环保。采用本发明专利技术所述的方法和原料制作出来的墙体砖，体密度达到0.4 g/cm3左右，抗压强度达到1.8‑2Mpa，热导率0.08 W/m.K，隔音效果达到40分贝。

Light high-strength wall brick and preparation method thereof

The invention discloses a high strength lightweight wall bricks, raw materials by weight were prepared by the silica sand 170 cement 80 190 copies, 90 copies, 45 copies of 35 lime, gypsum 17 24, ash 25 water 320 35 copies, 350 copies, 0.3 aluminum 0.5 copies, 30 copies of 25 mica powder. The foaming method of the invention is inorganic foaming, which has better corrosion resistance and fire prevention performance compared with the organic foaming, and is more environment-friendly. Wall brick and method of the invention comprises the raw materials produced, bulk density reached 0.4 around g/cm3, the compressive strength reached 1.8 2Mpa, thermal conductivity of 0.08 W/m.K, noise reached 40 decibels.

【技术实现步骤摘要】

本专利技术涉及建筑填充材料
，特别涉及一种发泡墙体砖及其制作方法。
技术介绍
正常室内隔墙都是用轻质的墙体砖，轻质砖其密度仅为600-700Kg/m3，轻质砖一般都是指发泡砖，目前比较多的发泡砖主要是采用有机发泡技术，有机发泡主要存在防腐性能和防火性能较差的缺点。轻质砖既能有效减小楼面负重，又具有良好的隔音效果，但轻质砖强度较差。如申请号为01310397200.0的中国专利公开了一种轻质墙体砖，该墙体砖的密度达到650Kg/m3，抗压强度仅为1.6Mpa。所以如何获得更轻更强的墙体砖是本行业内永远追求的课题。
技术实现思路
本专利技术要解决的技术问题是：针对现有的发泡砖密度过大和强度较低的问题，采用无机发泡的方法制作出了一种更轻更强的墙体砖。本专利技术的技术方案是：一种轻质高强度墙体砖，其制备时采用的原料重量份数为：硅沙190-210份，水泥80-100份，石灰35-45份，磷石膏17-24份，煤灰45-55份，水320-350份，铝粉0.3-0.5份，云母粉25-30份。云母粉的质量占总干重质量的7.5-8.5%。一、按照配比称重配料，将各物料磨成粉末状，温度36-40℃下混本文档来自技高网...

【技术保护点】
一种轻质高强度墙体砖，其特征在于制备时采用的原料重量份数为：硅沙190‑210份，水泥80‑100份，石灰35‑45份，磷石膏17‑24份，煤灰45‑55份，水320‑350份，铝粉0.3‑0.5份，云母粉25‑30份。

【技术特征摘要】
1.一种轻质高强度墙体砖，其特征在于制备时采用的原料重量份数为：硅沙190-210份，水泥80-100份，石灰35-45份，磷石膏17-24份，煤灰45-55份，水320-350份，铝粉0.3-0.5份，云母粉25-30份。2.根据权利要求要求1所述的轻质高强度墙体砖，其特征在于：云母粉的质量占总干重质量的7.5-8.5%。3.一种用于制备如权利要求2所述轻质高强度墙体砖的方法，其特征在于：一、...

【专利技术属性】
技术研发人员：董志斌，董德良，杨立勇，刘友群，谢治林，
申请(专利权)人：贵州虹懿环保建材有限公司，
类型：发明
国别省市：贵州;52