用于促进动物群和植物群生长的方法和基材技术

本发明专利技术提供用于促进水生环境中动物群和植物群的生长的包括具有小于12的pH的混凝土基材的海洋基础设施，以及用于促进水生环境中动物群和植物群(包括石内和石上植物群以及石内和石上厌氧和需氧动物群和植物群)的生长的方法。

【技术实现步骤摘要】
【国外来华专利技术】
本专利技术提供了用于促进陆生和水生环境中动物群和植物群的生长的方法。现有技术以下列出被认为作为背景与目前公开的主题相关的参考文献：BULLERI,F.&CHAPMAN,M.G.(2010)Theintroductionofcoastalinfrastructureasadriverofchangeinmarineenvironments.JournalofAppliedEcology,47,26-35.CHAPMAN,M.G.&UNDERWOOD,A.J.(2011)Evaluationofecologicalengineeringof\armoured\shorelinestoimprovetheirvalueashabitat.JournalofExperimentalMarineBiologyandEcology,400,302-313.CONNELL,S.D.&GLASBY,T.M.(1999)Dourbanstructuresinfluencelocalabundanceanddiversityofsubtidalepibiota？AcasestudyfromSydneyHarbour,Australia.MarineEnvironmentalResearch,47,373-387.DUGAN,J.E.,AIROLDI,A.,CHAPMAN,M.G.,WALKER,S.&SCHLACHER,T.(2011)Estuarineandcoastalstructures:environmentaleffects.Afocusonshoreandnearshorestructures.INWOLANSKI,E.,ELLIOTT,M.&DUGAN,J.E.(编辑)TreatiseonEstuarineandCoastalScience:8.Human-inducedproblems(usesandabuses).NewYork,ElsevierDYSON,K.L.(2009)HabitatEnhancingMarineStructures:Creatinghabitatinurbanwaters.MasterofMarineAffairsThesis.SchoolofMarineAffairs,CollegeofOceanandFisherySciences,UniversityofWashington.GLASBY,T.M.,CONNELL,S.D.,HOLLOWAY,M.G.&HEWITT,C.L.(2007)Nonindigenousbiotaonartificialstructures:couldhabitatcreationfacilitatebiologicalinvasions？MarineBiology,151,887-895.GOFF,M.(2010)EvaluatingHabitatEnhancementsofanUrbanIntertidalSeawall:EcologicalResponsesandManagementImplications.MScThesisUniversityofWashingtonJAYAKUMAR,S.&SARAVANANE,R.(2010)BiodeteriorationofCoastalConcreteStructuresbyMarineGreenAlgae.InternationalJournalofCivilEngineerng,8,352-361.JONES,C.G.,LAWTON,J.H.&SHACHAK,M.(1994)Organismsasecosystemengineers.Oikos,69,373-386.LAM,N.W.Y.,HUANG,R.&CHAN,B.K.K.(2009)VariationsinIntertidalassemblagesandzonationpatternsbetweenverticalartificialseawallsandnaturalrockyshores:AcasestudyfromVictoriaHarbour,HongKong.ZoologicalStudies,48,184-195.LI,B.,REEVE,D.E.&FLEMING,C.A.(2005)Designforenhancedmarinehabitatsincoastalstructures.ProceedingsoftheInstitutionofCivilEngineers-MaritimeEngineering,158,115-122.LUKENS,R.R.&SELBERG.,C.(2004)GuidelinesforMarineArtificialReefMaterials.AJointPublicationoftheGulfandAtlanticStatesMarineFisheriesCommissions.NAYLOR,L.A.,VENN,O.,COOMBES,M.A.,JACKSON,J.THOMPSON,R.C.(2011)IncludingEcologicalEnhancementsinthePlanning,DesignandConstructionofHardCoastalStructures:Aprocessguide.ReporttotheEnvironmentAgency(PID110461).UniversityofExeterPERKOL-FINKEL,S.,FERRARIO,F.,NICOTERA,V.&AIROLDI,L.(2012)Conservationchallengesinurbanseascapes:promotingthegrowthofthreatenedspeciesoncoastalinfrastructures.JournalofAppliedEcology,49,1457-1466.RISINGER,J.D.(2012)BiologicallyDominatedEngineeredCoastalBreakwaters.PhDThesis,.DepartmentofBiologicalandAgriculturalEngineering.LouisianaStateUniversityandAgriculturalandMechanicalCollege.SCOTT,P.J.B.,MOSER,K.A.&本文档来自技高网...

【技术保护点】
一种海洋基础设施，所述海洋基础设施包括具有小于12的pH的混凝土基材，所述海洋基础设施用于促进水生环境中动物群和植物群的生长。

【技术特征摘要】
【国外来华专利技术】2013.02.14 US 61/764,8001.一种海洋基础设施，所述海洋基础设施包括具有小于12的pH的
混凝土基材，所述海洋基础设施用于促进水生环境中动物群和植物群的生
长。
2.根据权利要求1所述的海洋基础设施，其中所述pH小于约11。
3.根据权利要求1或2所述的海洋基础设施，其中所述pH是在约9
至10.5之间。
4.根据前述权利要求中任一项所述的海洋基础设施，其中所述混凝
土基材的所述pH是所述基础设施的上表面的pH。
5.根据权利要求4所述的海洋基础设施，其中所述表面的厚度是约
5cm或更厚。
6.根据前述权利要求中任一项所述的海洋基础设施，其中水生环境
的盐度是在约0至45ppt之间。
7.根据前述权利要求中任一项所述的海洋基础设施，其中所述基础
设施具有粗糙等级为至少12的表面粗糙度。
8.根据前述权利要求中任一项所述的海洋基础设施，其中所述基础
设施具有RA值为至少50微米的表面粗糙度和RA值为5-20mm的表面
纹理。
9.根据前述权利要求中任一项所述的海洋基础设施，其中所述混凝
土基材具有约1100至约2500Kg/m3之间的重量/体积。
10.根据前述权利要求中任一项所述的海洋基础设施，其中所述混凝
土基材具有约1100至约1800Kg/m3之间的重量/体积。
11.根据前述权利要求中任一项所述的海洋基础设施，其中所述混凝
土基材包含0至约90％之间的波特兰水泥。
12.根据前述权利要求中任一项所述的海洋基础设施，其中所述混凝

\t土基材包含微硅/硅灰和偏高岭土和/或铝酸钙水泥的至少一种。
13.根据前述权利要求中任一项所述的海洋基础设施，其中所述混凝
土基材具有约30至约80MPa之间的平均抗压强度。
1...

【专利技术属性】
技术研发人员：希姆里特·芬克尔，伊多·赛拉，
申请(专利权)人：艾康克雷特科技有限公司，
类型：发明
国别省市：以色列;IL