一种防静电水泥地板漆制造技术

阅读:8 留言:0更新日期:2018-03-03 13:20
本发明专利技术公开了一种防静电水泥地板漆,各组份物质及其质量份数为:环氧树脂50~65%,邻羟基苯甲酸苯酯0.3~0.4%,润湿剂0.1~0.25%,气相法白炭黑0.2~0.4%,异辛酸铋0.2~0.6%,改性固化剂0.05~0.09%,云母粉6~12%,钛白粉9~12%,消泡剂0.2~0.4%,柠檬酸三丁酯0.2~0.6%,松节油2~4%,凹凸棒土6~9%,余量为水。具有良好的防静电能力,可以长期做到避免因静电引起的火灾和爆炸,从而保证人们的生命与财产安全。

Antistatic cement floor paint

The invention discloses an antistatic cement floor paint, the components of the material and quality portions: epoxy resin 50 ~ 65%, 2-hydroxy benzoic acid benzene ester 0.3 ~ 0.4%, 0.1 ~ 0.25% wetting agent, fumed silica 0.2 ~ 0.4%, 0.2 ~ 0.6% bismuth Ethylhexanoate, modified curing agent 0.05 ~ 0.09%, 6 ~ 12% mica powder, titanium dioxide is 9 ~ 12%, defoaming agent 0.2 ~ 0.4%, 0.2 ~ 0.6% and three citric acid ester, turpentine 2 ~ 4%, 6 ~ 9% attapulgite, balance of water. With good anti-static ability, it can avoid the fire and explosion caused by static electricity for a long time, so as to ensure the safety of people's life and property.

【技术实现步骤摘要】
一种防静电水泥地板漆
本专利技术涉及一种地板漆,特别是涉及一种防静电水泥地板漆。
技术介绍
近年来,中国涂料行业在迅速成长的房地产、汽车、船舶、等下游行业的推动下,以高速度增长,成为世界涂料生产和消费大国。涂料的种类繁多,地板漆就是其中一种应用较广泛的的涂料,而水泥地板漆则是地板其中应用较多的一种。对于一些轻、重工业工厂,需要走叉车、重载手推叉车、汽车等运输工具,这就要求地面有较大的耐磨性和较好的耐冲击力。由于摩擦的作用,易产生静电,而对于一些特殊的场所,静电的产生就有可能引发火星,从而引起火灾或爆炸,而一旦产生爆炸,工厂及工作人员都会毁于一旦。所以,对于工厂来说,防静电是一种保护财产、生命安全的非常重要的手段。
技术实现思路
为了解决上述技术问题,本专利技术通过改进原料组份及质量配比,可以提供一种具有良好的防静电性能的水泥地板漆,耐磨性高,可以有效防止静电的产生,从而避免因静电引起的火灾和爆炸,保证人们的生命与财产安全。本专利技术完整的技术方案包括:一种防静电水泥地板漆,其特征在于,各组份物质及其质量份数为:环氧树脂50~65%,邻羟基苯甲酸苯酯0.3~0.4%,润湿剂0.1~0.25%,气相法白炭黑0.2~0.4%,异辛酸铋0.2~0.6%,改性固化剂0.05~0.09%,云母粉6~12%,钛白粉9~12%,消泡剂0.2~0.4%,柠檬酸三丁酯0.2~0.6%,松节油2~4%,凹凸棒土6~9%,余量为水。优选的,各组份物质及其质量百分比为:环氧树脂53~62%,邻羟基苯甲酸苯酯0.3~0.4%,润湿剂0.2~0.25%,气相法白炭黑0.25~0.35%,异辛酸铋0.3~0.5%,改性固化剂0.06~0.08%,云母粉7~11%,钛白粉10~11%,消泡剂0.25~0.35%,柠檬酸三丁酯0.3~0.5%,松节油2.5~3.5%,凹凸棒土7~8%,余量为水。优选的,各组份物质及其质量百分比为:环氧树脂55%,邻羟基苯甲酸苯酯0.3%,润湿剂0.23%,气相法白炭黑0.28%,异辛酸铋0.35%,改性固化剂0.07%,云母粉8%,钛白粉10%,消泡剂0.25%,柠檬酸三丁酯0.4%,松节油2.7%,凹凸棒土7.5%,余量为水。本专利技术的有益效果:本专利技术制得的水泥地板漆耐磨性高,表面电阻为8×108欧姆至10×108,具有良好的防静电作用。具体实施方式实施例1:一种防静电水泥地板漆,各组份物质及其质量份数为:环氧树脂50%,邻羟基苯甲酸苯酯0.3%,润湿剂0.1%,气相法白炭黑0.2%,异辛酸铋0.2%,改性固化剂0.069%,云母粉7%,钛白粉9%,消泡剂0.2%,柠檬酸三丁酯0.2%,松节油2%,凹凸棒土6%,余量为水。实施例2:一种防静电水泥地板漆,各组份物质及其质量百分比为:环氧树脂63%,邻羟基苯甲酸苯酯0.4%,润湿剂0.25%,气相法白炭黑0.35%,异辛酸铋0.5%,改性固化剂0.08%,云母粉11%,钛白粉11%,消泡剂0.35%,柠檬酸三丁酯0.5%,松节油3.5%,凹凸棒土8%,余量为水。实施例3:一种防静电水泥地板漆,各组份物质及其质量百分比为:环氧树脂55%,邻羟基苯甲酸苯酯0.3%,润湿剂0.23%,气相法白炭黑0.28%,异辛酸铋0.35%,改性固化剂0.07%,云母粉8%,钛白粉10%,消泡剂0.25%,柠檬酸三丁酯0.4%,松节油2.7%,凹凸棒土7.5%,余量为水。实施例4:一种防静电水泥地板漆,各组份物质及其质量百分比为:环氧树脂58%,邻羟基苯甲酸苯酯0.38%,润湿剂0.23%,气相法白炭黑0.32%,异辛酸铋0.47%,改性固化剂0.08%,云母粉10%,钛白粉10.5%,消泡剂0.3%,柠檬酸三丁酯0.45%,松节油2.7%,凹凸棒土7.8%,余量为水。以上所述为本专利技术的较佳实施例,凡依本专利技术申请专利范围所做的等同变化,皆应属于本专利技术的保护范围。本文档来自技高网...

【技术保护点】
一种防静电水泥地板漆,其特征在于,各组份物质及其质量百分比为:环氧树脂50~65%,邻羟基苯甲酸苯酯0.3~0.4%,润湿剂0.1~0.25%,气相法白炭黑0.2~0.4%,异辛酸铋0.2~0.6%,改性固化剂0.05~0.09%,云母粉6~12%,钛白粉9~12%,消泡剂0.2~0.4%,柠檬酸三丁酯0.2~0.6%,松节油2~4%,凹凸棒土6~9%,余量为水。

【技术特征摘要】
1.一种防静电水泥地板漆,其特征在于,各组份物质及其质量百分比为:环氧树脂50~65%,邻羟基苯甲酸苯酯0.3~0.4%,润湿剂0.1~0.25%,气相法白炭黑0.2~0.4%,异辛酸铋0.2~0.6%,改性固化剂0.05~0.09%,云母粉6~12%,钛白粉9~12%,消泡剂0.2~0.4%,柠檬酸三丁酯0.2~0.6%,松节油2~4%,凹凸棒土6~9%,余量为水。2.一种防静电水泥地板漆,其特征在于,各组份物质及其质量百分比为:环氧树脂53~62%,邻羟基苯甲酸苯酯0.3~0.4%,润湿剂0.2~0.25%,气相法白炭黑...