本发明专利技术涉及一种乳胶漆面漆及其制备方法，特别涉及一种免稀释一次涂刷成型乳胶漆面漆及其制备方法，属于建筑装饰用涂料领域。它由以下原料按以下重量配比配制而成：水20-29份、二醇类防冻剂1-2份、纤维素0.1-0.2份、膨润土0.05-0.2份、分散剂0.7-1份、润湿剂0.1-0.2份、矿物油消泡剂0.2-0.6份、碱性pH调节剂0.1-0.2份、钛白粉15-22份、煅烧高岭土8-10份、闪烧高岭土0-5份、颜填料15-25份、防霉剂0.2-0.5份、乳液15-20份、成膜助剂1-2份、防腐剂0.1-0.5份、增稠剂1计0.1-0.3份、增稠剂2计1-2份。

Non dilution once brushing forming latex paint top coat and preparation method thereof

The invention relates to a latex paint finish and a preparation method thereof, in particular to a latex paint finish without dilution and brushing at one time and a preparation method thereof, belonging to the field of architectural decoration coating. It consists of the following raw materials according to the weight proportion: 20-29 portions of water and glycol antifreeze agent 1-2, cellulose 0.1-0.2, bentonite, 0.05-0.2, dispersion agent 0.7-1, wetting agent 0.1-0.2, mineral oil defoamer 0.2-0.6, alkaline pH regulator 0.1-0.2, titanium dioxide 15-22, calcined kaolin 8-10, a 0-5, a flash burning kaolin pigment 15-25, fungicide 0.2-0.5 parts, 15-20 parts, emulsion film-forming additives, preservatives, 1-2 0.1-0.5 thickening agent 1 0.1-0.3, a thickening agent 2 1-2.

【技术实现步骤摘要】

【技术保护点】
一种免稀释一次涂刷成型乳胶漆面漆，其特征在于：它由以下原料按以下重量配比配制而成：所述增稠剂1采用中或中低剪切类的碱溶胀类或聚氨酯类增稠剂；所述增稠剂2采用高剪切类聚氨酯增稠剂或高剪切类聚醚类增稠剂。FDA0000389460520000011.jpg

【技术特征摘要】

【专利技术属性】
技术研发人员：洪杰，杨静，林昌庆，林伟，
申请(专利权)人：三棵树涂料股份有限公司，
类型：发明
国别省市：