本发明专利技术公开了一种抗霉除甲醛涂料，该涂料的组成配比(按重量计)如下：聚苯乙烯-丙烯酸共聚物或聚丙烯酸共聚物或聚醋酸乙烯-丙烯酸共聚物100份，滑石粉26-30份，助剂5-8份，颜料6-10份，防霉杀菌剂8-10份，吸附剂3-5份，水40-50份，所述防霉杀菌剂为纳米TiO2、纳米ZnO和ZrO2的混合物，纳米TiO2、纳米ZnO的粒度均为30～50纳米，ZrO2的粒度为-400目，三者的比例为TiO2：ZnO：ZrO2＝（1～2）：1：0.5。本发明专利技术的涂料能有效的抵抗霉变，并且效果持久，同时该涂料兼具有清除甲醛的作用。

Mildew resistant formaldehyde removing paint

The invention discloses a mildew resistant coating composition in addition to formaldehyde, the coating (by weight) as follows: styrene - acrylic acid copolymer or polyacrylic acid copolymer or poly vinyl acetate acrylic copolymer 100, talcum powder 26-30, 5-8 additives, pigment 6-10, anti mildew fungicide 8-10, adsorbent 3-5, water 40-50, the mixture of bactericide for nano TiO2, ZnO and ZrO2, the size of nano TiO2, nano ZnO was 30 ~ 50 nm, and the particle size of ZrO2 was -400, the proportion of three for TiO2:ZnO:ZrO2 = (1 ~ 2): 1:0.5. The paint of the invention can effectively resist mildew, and has a lasting effect, and simultaneously, the coating has the function of removing formaldehyde.

【技术实现步骤摘要】

【技术保护点】
一种抗霉除甲醛涂料，其特征在于，该涂料的组成配比(按重量计)如下：聚苯乙烯?丙烯酸共聚物或聚丙烯酸共聚物或聚醋酸乙烯?丙烯酸共聚物100份，滑石粉26?30份，助剂5?8份，颜料6?10份，防霉杀菌剂8?10份，吸附剂3?5份，水40?50份，所述防霉杀菌剂为纳米TiO2、纳米ZnO和ZrO2的混合物，纳米TiO2、纳米ZnO的粒度均为30～50纳米，ZrO2的粒度为?400目，三者的比例为TiO2：ZnO：ZrO2＝（1～2）：1：0.5。

【技术特征摘要】

【专利技术属性】
技术研发人员：李聚刚，钱振宇，陈晓龙，
申请(专利权)人：苏州市姑苏新型建材有限公司，
类型：发明
国别省市：