一种金属阴极电泳前多金属氧酸稀土盐—硅烷化处理工艺制造技术

本发明专利技术公开了一种金属阴极电泳前多金属氧酸稀土盐-硅烷化处理工艺，运用阴极电泳前稀土-硅烷化处理技术，即通过多金属氧酸盐合成技术与硅烷化处理技术成功融合，使得合成的硅钼杂多酸稀土镧盐与硅烷膜杂化，在金属表面形成硅烷-硅钼杂多酸稀土镧杂化膜。本发明专利技术工艺所得的杂化膜具有耐腐蚀性能强，致密均匀，电阻小，附着力好，“自修复”性能好等优点。

Process for treating rare earth salt of rare earth metal acid prior to metal cathode electrophoresis

The invention discloses a metal cathode electrophoresis before polyoxometalates with rare earth salt - silane treatment process, the use of cathodic electrophoresis before rare earth silane treatment technology, namely by polyoxometalates synthesis technology and silane treatment technology integration, makes the silicon molybdenum heteropoly acid lanthanum salt and silane hybrid film synthesis. The formation of silane - silicon molybdenum heteropoly acid lanthanum hybrid film on metal surface. The hybrid film obtained by the invention has the advantages of strong corrosion resistance, compactness, uniformity, small resistance, good adhesion, good self repairing performance, etc..

【技术实现步骤摘要】

【技术保护点】
１．一种金属阴极电泳前稀土多金属氧酸盐－硅烷化处理工艺，其特征在于：运用阴极电泳前稀土－硅烷化处理技术，即通过多金属氧酸盐合成技术与硅烷化处理技术成功融合，使得合成的硅钼杂多酸稀土镧盐与硅烷膜杂化，在金属表面形成硅烷－硅钼杂多酸稀土镧杂化膜，具体包括以下步骤：（１）首先将金属材料表面进行脱脂处理；（２）将脱脂处理的金属材料进行两次水洗；（３）将水洗后的金属材料进行抛光处理，再次水洗；（４）将步骤（３）处理的金属材料用碱液进清洗，然后再次水洗；（５）将步骤（４）水洗后的金属材料放入盛有硅烷剂的硅烷槽里浸渍，进行硅烷化处理，浸泡完成后，在金属材料表面得到硅烷－硅钼杂多酸稀土镧杂化膜，要求，浸泡时间１－３ｍｉｎ，浸泡温度为室温～４０℃，纯水洗电导率＜２０μｓ／ｃｍ。（６）将硅烷化处理后的金属材料在５０－１００℃下烘干固化０．５－１ｈ。

【技术特征摘要】

【专利技术属性】
技术研发人员：庞志成，丁宁，陈云帮，丁甸，刘传让，徐大力，
申请(专利权)人：蚌埠市钰诚五金工贸有限公司，
类型：发明
国别省市：34