镁及镁合金晶粒细化剂及其制备方法技术

本发明专利技术属于金属合金技术领域，涉及一种镁及镁合金晶粒细化剂，所述晶粒细化剂为铝-锆-碳（Al-Zr-C）中间合金，其化学成分的重量百分比为：0.01%～10%的Zr、0.01%～0.3%的C，余量为Al。本发明专利技术还公开了这种晶粒细化剂的制备方法。本发明专利技术的晶粒细化剂是一种形核能力强从而具有优良的细化镁及镁合金晶粒能力的中间合金，这种晶粒细化剂可工业应用于镁及镁合金型材的铸造轧制，为镁在工业上的广泛应用提供了可能。

Magnesium and magnesium alloy grain fining agent and preparation method thereof

The invention belongs to the technical field of metal alloy, relates to a magnesium and magnesium alloy grain refiner, the grain refining agent for aluminum zirconium carbon (Al-Zr-C) alloy, the chemical composition of the weight percentage: 0.01% to 10% Zr and 0.01% ~ 0.3% C, the rest is Al. The invention also discloses the preparation method of the grain refiner. The grain refinement agent of the invention is an intermediate alloy nucleation ability which has refined magnesium and magnesium alloy grain fine, the grain refinement can be applied to industrial rolling casting of magnesium and magnesium alloy profiles, provides the possibility for its wide application in industry.

【技术实现步骤摘要】

本专利技术涉及一种通过细化晶粒来改善金属及合金性能的中间合金，尤其是一种用 于镁及镁合金的晶粒细化剂及其制备方法。
技术介绍
镁及镁合金的工业应用始于20世纪30年代，由于镁及镁合金是目前最轻的金 属结构材料，具有密度低、比强度和比刚度高、阻尼减震性好、导热性好、电磁屏蔽效果佳、 机加工性能优良、零件尺寸稳定、易回收等优点，使镁及镁合金特别是变形镁合金在交通工 具、工程结构材料和电子领域等中的应用潜力非常巨大。变形镁合金是指可用挤压、轧制、 锻造等塑性成型方法加工成形的镁合金。然而，由于受到材料制备、加工技术、抗腐蚀性能 以及价格等因素制约，镁合金尤其是变形镁合金的应用量远远落后于钢铁和铝合金，在金 属材料领域里还没有任何一种材料像镁那样，其发展潜力和实际应用现状之间存在如此大 的差异。镁与铁、铜、铝等常用的金属不同，镁合金是密排六方晶体结构，室温下只有3个 独立的滑移系，合金的塑性变形能力较差，其晶粒大小对力学性能影响十分显著。镁合金结 晶温度范围较宽，热导率较低，体收缩较大，晶粒粗化倾向严重，凝固过程中易产生缩松、热 裂等缺陷；细小的晶粒有助于减少缩松、减小第二相的大小和改善铸本文档来自技高网...

【技术保护点】
１．一种镁及镁合金晶粒细化剂，其特征在于：所述晶粒细化剂为铝－锆－碳中间合金，其化学成分的重量百分比为：０．０１％～１０％的Ｚｒ、０．０１％～０．３％的Ｃ，余量为Ａｌ。

【技术特征摘要】

【专利技术属性】
技术研发人员：陈学敏，叶清东，余跃明，李建国，
申请(专利权)人：新星化工冶金材料深圳有限公司，
类型：发明
国别省市：94