抗菌消炎凡士林纱布，在纱布上涂有含药凡士林，含药凡士林配方为，按重量计凡士林∶三溴酚泌∶石蜡∶SEBS∶乳化剂＝100∶3～10∶5～10∶5～10∶2～5，所述纱布为醋酸纤维纱布。抗菌消炎凡士林纱布生产工艺，1)、按重量计将100份凡士林与3～10份三溴酚泌在40℃～70℃进行研磨搅拌2～5h后，加入2～5份乳化剂搅拌1～3h，然后加入5～10份石蜡和5～10份SEBS后继续搅拌2～4h得到凡士林油混合物，2)、将检验合格的凡士林油混合物定量涂覆到纱布上得到抗菌消炎凡士林纱布，涂覆量为120～300g/m2，3)、将抗菌消炎凡士林纱布在40℃～60℃的温度条件下消毒、灭菌4～6h即得成品。它可有效防止伤口感染，同时可保持伤口湿润，营造湿性环境，促进伤口愈合。

Antibacterial and antiphlogistic Vaseline gauze and its production process

Antibacterial and antiphlogistic Vaseline gauze, gauze coated with Vaseline Vaseline containing, containing formula, by weight: three Vaseline bromophenol: urinary wax: SEBS: emulsifier = 100: 3 to 10: 5 to 10: 5 to 10: 2 to 5, the acetate fiber gauze gauze. Antibacterial Vaseline gauze production process, 1), by weight of 100 and 3 to 10 portions of three Vaseline bromophenol urinary at 40 to 70 DEG C for grinding stirring after 2 ~ 5h, 2 ~ 5 mixing emulsifier added 1 ~ 3H, and then adding 5 ~ 10 and 5 ~ 10 SEBS paraffin after stirring 2 ~ 4H to vaseline oil mixture, 2), the vaseline oil mixture quantitative inspection of the coating to the gauze has antibacterial anti-inflammatory Vaseline gauze, coating amount is 120 ~ 300g/m2, 3), the antibacterial and anti-inflammatory Vaseline gauze at 40 DEG C to 60 DEG C under the temperature condition of disinfection and sterilization in 4 ~ 6h the product is made. It can effectively prevent wound infection, while keeping the wound moist, creating a wet environment, and promote wound healing.

【技术实现步骤摘要】

【技术保护点】
１．抗菌消炎凡士林纱布，包括纱布，其特征在于：在纱布上涂有含药凡士林，含药凡士林配方为，按重量计凡士林∶三溴酚泌∶石蜡∶ＳＥＢＳ∶乳化剂＝１００∶３～１０∶５～１０∶５～１０∶２～５，所述纱布为醋酸纤维纱布。

【技术特征摘要】

【专利技术属性】
技术研发人员：张新强，曹黎明，付开，胡修元，沈博强，宋九星，
申请(专利权)人：绍兴振德医用敷料有限公司，
类型：发明
国别省市：33