一种改进型异种钢管机械焊对接接头坡口制造技术

本发明专利技术提供了一种改进型异种钢管机械焊对接接头坡口，在不锈钢管侧与高合金耐热钢管分别有一个角度α的坡口，其特征在于，在不锈钢管侧带有长度为ａ，厚度为ｂ的突台，在高合金耐热钢管侧带有长度为ｃ，厚度为ｂ的突台，其中０≤ｃ＜ａ。本发明专利技术的优点是：配合采用一定的焊接工艺参数即能使焊缝根部镍含量达到４０％以上；焊缝机械性能等各方面性能均与一般坡口对接焊缝无异；坡口加工简便，采用车床进行机加工或者制作相应的刀具进行一次成形倒角即可成形。

Improved groove joint groove for mechanical welding of dissimilar steel pipe

The present invention provides an improved steel mechanical welding butt joint groove, the stainless steel tube side and high heat-resistant alloy steel tube are respectively provided with a groove angle, which is characterized in stainless steel pipe with side length of a, thickness of Taiwan B, in high heat-resistant alloy steel tube with a side length of C the thickness of B, Taiwan, 0 < C < a. The invention has the advantages that: with the use of certain welding parameters which can make the weld nickel content of more than 40%; and the general butt weld mechanical properties of weld groove is; the processing is convenient, using lathe for machining or making the corresponding tool for forming a chamfer can be formed.

【技术实现步骤摘要】

本专利技术涉及一种改进型异种钢管机械焊对接接头坡口，用于高合金耐热钢管与不锈钢管的机械焊对接焊接。
技术介绍
高合金耐热钢管与不锈钢管对接坡口一般采用带一定角度且对称的坡口型式。该 坡口型式的对接焊缝的根部镍含量一般低于40%，异种钢对接接头焊缝根部镍含量低于 40%会导致锅炉运行时该部位的被腐蚀量大于其他部位，使该处管壁壁厚减薄量大于其他 部位，而带来造成爆管的可能性。
技术实现思路
本专利技术的目的是提供一种可以使得根部镍含量大于40%的对接接头坡口 。 为了达到上述目的，本专利技术的技术方案是提供了一种改进型异种钢管对接接头坡 口，在不锈钢管侧与高合金耐热钢管分别有一个角度a的坡口，其特征在于，在不锈钢管 侧带有长度为a，厚度为b的突台，在高合金耐热钢管侧带有长度为c，厚度为b的突台，其 中0《c < a。 进一步，所述长度a为3mm 5mm，厚度b为lmm 2mm，长度c为0 2mm。所述 角度a为5° 10° 。 本专利技术采用了不对称的对接接头坡口，不锈钢管与高合金耐热钢管坡口角度均为 a ，该角度应尽可能小，以增加焊接过程中填充金属的熔敷量。不锈钢管一侧与合金本文档来自技高网...

【技术保护点】
一种改进型异种钢管机械焊对接接头坡口，在不锈钢管（１）侧与高合金耐热钢管（２）分别有一个角度α的坡口，其特征在于，在不锈钢管（１）侧带有长度为ａ，厚度为ｂ的突台，在高合金耐热钢管（２）侧带有长度为ｃ，厚度为ｂ的突台，其中０≤ｃ＜ａ。