The invention discloses a method for reducing impurity content of 2-methyl naphthalene, coal tar extraction with the content of not less than 96% 2 - methyl naphthalene as raw materials by melt crystallization method, which comprises the following steps: (1) in the mould and adding 2 methyl naphthalene raw material, gradually heating, the mold temperature rise 60 to 70 DEG C, the 2 - methyl naphthalene raw material in the mold of the melt in the mould; (2) 2 - methyl naphthalene raw material after melting, slow cooling, the cooling crystallization temperature of the reactor to 30 to 31 DEG C, the cooling crystallization process lasts 3 to 4.5 hours; (3) without crystallization emissions in the crystallizer the remaining material, crystal is purified 2 - methyl naphthalene. The method can effectively reduce the content of impurities such as 1 - methyl naphthalene, indole, 2 - methyl thiophene thiophene, 5 - methyl thiophene thiophene in 2 - methyl methyl, and has a high recovery rate and is clean and environment-friendly.
【技术实现步骤摘要】
本专利技术涉及，具体涉及去除2-甲基萘中的 l-甲基萘、吲哚、苯并噻吩类等杂质的方法。
技术介绍
2-甲基萘(又名e-甲基萘；英文名2-methylnaphthalene;分子式C H10; 分子量142.20; CAS号91-57-6)是一种重要的有机化工原料，可用于生产纺织 助剂、润滑剂和植物生长调节剂，高纯度的2-甲基萘是合成维生素K类药物和饲料 添加剂的原料。随着近些年医药和饲料工业的发展，国际上对2-甲基萘的质量要求 越来越高，需求量也越来越大。日本川崎钢铁公司建成了以吸收油(洗油)为原料生产2—甲基萘的半工业化车 间，利用共沸精馏、加氢脱硫、再精馏、异构化技术生产2—甲基萘。共沸精馏选 用乙二醇、二甘醇或乙醇胺为共沸剂，共沸剂与2—甲基萘的物质的量比为1. 34， 共沸精馏可除去原料中的含氮化合物，用加氢的方法去除原料中的含硫化合物；在 精馏工段，脱除烷基苯类、甲基四氢化萘、2—甲基萘、联苯等组分；在异构化工 段，去除循环油中的萘和2—甲基萘等组分。通过精馏可以得到高纯度的2—甲基萘。Osaka公司提出先蒸馏再用酸萃取的方法提纯甲基萘，采用传统方法在...
【技术保护点】
一种降低２－甲基奈杂质含量的方法，以煤焦油中提取的含量不低于９６％的２－甲基萘为原料，其特征在于，包括如下步骤： （１）在结晶器内中加入２－甲基萘原料，逐步升温加热，将结晶器温度升至６０～７０℃，使得结晶器中的２－甲基萘原料全部融化； （２）结晶器中２－甲基萘原料全部融化后，以８～１３℃／ｈ的速率降温，将结晶器温度冷却至３０～３１℃，整个冷却结晶过程持续３～４．５小时； （３）排放结晶器中未结晶的物质，剩余的结晶物即为纯化后的２－甲基萘。
【技术特征摘要】
【专利技术属性】
技术研发人员：袁康入，
申请(专利权)人：上海宝钢化工有限公司，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。