The invention discloses a transparent flame retardant polycarbonate (PC) material and preparation method thereof, wherein the material comprises by weight the following raw materials: PC (45 ~ 55 melting point 22), PC (44 ~ 54 melting point 5), PTFE powder is 0.2 ~ 0.6, flame retardant 0.04 ~ 0.12, 0.2 ~ release agent 0.8, the invention uses two different specifications of the melting point of PC resin, flame retardant (perfluorocarbon potassium) and release agent for extrusion production according to the specific technological conditions by the double screw with the 9 temperature zone of the extruder, can be prepared by UL 94 test standard test of flame retardant transparent poly carbon acid V0 (PC) materials, and simple preparation process, low preparation cost.
【技术实现步骤摘要】
本专利技术涉及阻燃工程塑料，特别涉及一种透明阻燃聚碳酸酯(PC)材料及其制备方法。
技术介绍
作为五大工程塑料之一的聚碳酸酯，是一种无定形、无嗅、无味、无毒、透明的热塑性聚合物，是唯一具有良好透明性的塑料品种，并且具有较好的机械强度、耐热性能及耐电综合性能，同时，还具有耐冲击强度高，蠕变性小，制品尺寸稳定，易增强，无毒卫生，能着色，性价比高，可化学修饰和物理改性潜力大等优点，广泛应用于玻璃装配业、汽车工业、电子、电器工业、工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜、休闲和防护器材等领域。 随着市场竞争的日益激烈，各行各业对聚碳酸酯(PC)各方面的性能提出了更高的要求，普通聚碳酸酯(PC)已经难以满足行业需求，但可以根据需求对聚碳酸酯(PC)进行改性，使其适应不同的需求。近年来，上述行业中许多都对聚碳酸酯(PC)材料的阻燃性提出了较高要求，以提高其产品的防火耐热性能，现有聚碳酸酯(PC)材料中，阻燃性通过UL-94测试标准能达到V0级别的并不多见，而且普遍存在制备工艺复杂，制备成本高的缺点。 针对上述不足，需探索一种简单工艺即可制备的阻燃聚碳酸...
【技术保护点】
一种透明阻燃聚碳酸酯（ＰＣ）材料，其特征在于：按重量份包括以下原料： ＰＣ（熔指２２） ４５～５５ ＰＣ（熔指５） ４４～５４ ＰＴＦＥ粉 ０．２～０．６ 阻燃剂 ０．０４～０．１２ 脱模剂 ０．２～０．８。
【技术特征摘要】
一种透明阻燃聚碳酸酯(PC)材料，其特征在于按重量份包括以下原料PC(熔指22)45～55PC(熔指5) 44～54PTFE粉0.2～0.6阻燃剂0.04～0.12脱模剂0.2～0.8。2. 根据权利要求1所述的透明阻燃聚碳酸酯(PC)材料，其特征在于按重量份包括以 下原料PC(熔指22) 50 PC(熔指5) 49 PTFE粉 0. 2阻燃剂 0.08脱模剂 0.5。3. 根据权利要求2所述的透明阻燃聚碳酸酯(PC)材料，其特征在于所述阻燃剂为全 氟丁基磺酸钾阻燃剂。4. 根据权利要求3所述的透明阻燃聚碳酸酯(PC)材料，其特征在于所述脱模剂为季 戊四醇硬脂酸酯。5. 制备权利要求1所述的透明阻燃聚碳酸酯(PC)材料的...
【专利技术属性】
技术研发人员：王铄，姚富，
申请(专利权)人：重庆启蓝塑料有限公司，
类型：发明
国别省市：85[中国|重庆]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。