The present invention provides a method for manufacturing a variable bar code information, which is characterized in that the method comprises the following steps: Step 1, the film in a full version of coated release agent; step 2, printing variable information on the film; step 3, the variable information of the spot with transfer material. The present invention uses digital printing mode existing barcode printing variable information obtained on the film, variable bar code information variable information code the same effect is obtained with the use of digital printers or printers, thus providing a ready-made barcode as no variable information digital printing equipment manufacturers. These manufacturers only need to use the existing heat transfer technology to transfer the variable information barcode to the desired product position, without adding additional equipment, thereby improving production efficiency and reducing costs.
【技术实现步骤摘要】
本专利技术涉及信息码及其制作方法,尤其涉及可变信息码及其制作方法。
技术介绍
目前,在传统的包装材料上获得的可变信息码,包括可变一维码、可变二 维码等条码,都要通过喷码或者条码打印设备来实现。但这些打印设备不但价 格昂贵,而且在操作过程中会有很多的问题出现,设备维护费用高,耗材价格 也比较昂贵,同时,在打印时会碰到不能准确的将条码打印到所需要打印的位 置的问题。在没有喷码或者条码打印设备的厂家,就无法自行在产品上打印可 变信息码,而要购买打印设备又要花费一笔额外的费用。
技术实现思路
为了解决上述问题,本专利技术提供了一种可变信息条码的制作方法,包括以下步骤步骤l,在薄膜上满版涂离型剂;步骤2,在薄膜上印刷可变信息;步骤3,在有可变信息的地方涂转印材料。所述步骤3之后还包括步骤4,将可变信息转印到承印物上。所述薄膜为聚对苯二甲酸乙二醇酯PET透明膜。所述转印材料为热熔胶。本专利技术还提供了一种可变信息条码,包括薄膜;薄膜上的离型层; 离型层上的印刷层;印刷层上的转印层。所述薄膜为聚对苯二甲酸乙二醇酯PET透明膜。 所述转印层为热熔胶。与现有技术相比,本专利技术具有以下有益效果本专利技术利用现有的数码印刷方式在薄膜上印刷所荻得的可变信息条码,与 使用数码打印机或喷码机获得的可变信息码同样效果的可变信息条码,从而为 没有数码打印设备的厂家提供了 一种现成的可变信息条码。这些厂家只需利用 现有的热转移:忮术将可变信息条码转移到所需的产品位置即可,不需要另外招: 入设备,提高了生产效率,同时降低了成本。附图说明图1为本专利技术的制作可变信息条码的流程图; 图2为本 ...
【技术保护点】
一种可变信息条码的制作方法,其特征在于,包括以下步骤: 步骤1,在薄膜上满版涂离型剂; 步骤2,在薄膜上印刷可变信息; 步骤3,在有可变信息的地方涂转印材料。
【技术特征摘要】
1. 一种可变信息条码的制作方法,其特征在于,包括以下步骤步骤1,在薄膜上满版涂离型剂;步骤2,在薄膜上印刷可变信息;步骤3,在有可变信息的地方涂转印材料。2. 如权利要求1所述的可变信息条码的制作方法,其特征在于,所述步 骤3之后还包括步骤4,将可变信息转印到承印物上。3. 如权利要求1所述的可变信息条码的制作方法,其特征在于,所述薄 膜为聚对苯二曱酸乙二醇酯...