The invention relates to the field of optoelectronic materials, in particular to a preparation method for batch synthesis of UV colloidal zinc sulfide quantum dots. The preparation method of the ultraviolet colloidal zinc sulfide quantum dot comprises the steps of solution configuration, synthesis reaction and centrifugal washing. The method of the invention uses zinc acetate as raw material to prepare colloidal ZnS quantum dot microsphere with narrow particle size distribution under low temperature, and the colloidal quantum dot solution is easy to self assemble into ZnS quantum dot film, which is suitable for being a photosensitive layer material of optoelectronic devices.
【技术实现步骤摘要】
紫外胶体硫化锌量子点的液相制备方法
本专利技术涉及光电子材料领域，尤其是一种可批量合成紫外胶体硫化锌量子点的液相制备方法。
技术介绍
作为新一代的半导体纳米材料，量子点由于自身的五大物理特性，如：量子表面效应、量子尺寸效应、量子隧道效应、量子限域效应以及库仑阻塞效应，而在生物医学、半导体光电器件、分析化学、太阳能电池等方面具有广泛的应用价值。ZnS是II-Ⅵ族化合物半导体，属于直接宽带隙半导体锌类化合物量子点，立方结构ZnS的带隙能是3.72eV，相比PbSe、CdTe等含铅元素和镉元素的量子点，ZnS量子点的原材料丰富，经济且毒性低，并且对环境无污染。在光电调节器、光传导器、光感应器、光催化等光学装置方面有着良好的应用前景，是目前材料科学研究的热点。目前量子点的制备方法有化学共沉淀法、原位法、水热法、微波法等，这些方法各有优劣，但就合成条件来说，一般都需要高温、高压、气氛保护等条件，且所需要的合成设备价格昂贵，存在实验条件苛刻，合成时间长，对环境存在危害等不足。
技术实现思路
针对现有硫化锌量子...
【技术保护点】
1.紫外胶体硫化锌量子点的液相制备方法，包括溶液的配置、合成反应、离心洗涤步骤，其特征在于具体制备步骤如下：/nS1，硫化钠和乙酸锌固体配置成小于0.005mol/L的溶液，形成锌离子前躯体溶液和硫离子前躯体溶液；/nS2，十二烷基磺酸钠(SDS)配置为临界胶束浓度溶液作为表面活性剂；/nS4，量取同体积比的SDS溶液与两种前躯体溶液，分别充分混合，形成锌离子前躯体混合溶液和硫离子前躯体混合溶液；/nS5，在常压，18-85℃下，磁力搅拌条件下，将硫离子前躯体混合溶液逐滴滴入锌离子前躯体混合溶液中，当两者体积比为达到1：1时，稳定反应至少10min，冷却到室温，得到乳白色硫...
【技术特征摘要】
1.紫外胶体硫化锌量子点的液相制备方法，包括溶液的配置、合成反应、离心洗涤步骤，其特征在于具体制备步骤如下：
S1，硫化钠和乙酸锌固体配置成小于0.005mol/L的溶液，形成锌离子前躯体溶液和硫离子前躯体溶液；
S2，十二烷基磺酸钠(SDS)配置为临界胶束浓度溶液作为表面活性剂；
S4，量取同体积比的SDS溶液与两种前躯体溶液，分别充分混合，形成锌离子前躯体混合溶液和硫离子前躯体混合溶液；
S5，在常压，18-85℃下，磁力搅拌条件下，将硫离子前躯体混合溶液逐滴滴入锌离子前躯...
【专利技术属性】
技术研发人员：唐利斌，李汝劼，赵清，郭小鹏，邢一山，吴圣娟，
申请(专利权)人：昆明物理研究所，
类型：发明
国别省市：云南;53