The invention provides a composite sandwich color steel plate, which has good fireproof performance. The utility model comprises a polyurethane core material and a color steel plate base material outside the polyurethane core material, and a ceramic fiber board is arranged between the polyurethane core material and the color steel plate base material. In addition, there are wave shaped pneumatic rubber sheets and arc holes in the middle of polyurethane core to improve impact resistance and sound insulation. Moreover, when preparing polyurethane core material, adding expanded graphite in situ polymerization of two ethyl hypophosphite as flame retardant can greatly improve the fireproof performance of core material, thereby further improving the fire resistance of the colored steel sheet. \u3002
【技术实现步骤摘要】
复合夹心彩钢板
本专利技术涉及彩钢板
，具体为复合夹心彩钢板。
技术介绍
随着科技的进步、人们环保意识的增强，彩钢板在各行各业的应用越来越受到推崇。其中，以硬质聚氨酯泡沫塑料为芯材的彩钢板最具有代表性。这种彩钢板与其他彩钢板相比，其保温隔热性能更好；但是，由于芯材为硬质聚氨酯泡沫塑料，所以极易燃烧，耐火等级极低，无法应用于一些防火等级比较高的领域。
技术实现思路
针对传统彩钢板阻燃性差的问题，本专利技术提供了复合夹心彩钢板，其防火性能好。其技术方案是这样的：复合夹心彩钢板，其包括聚氨酯芯材和位于所述聚氨酯芯材外侧的彩钢板基材，其特征在于：所述聚氨酯芯材和所述彩钢板基材之间设有陶瓷纤维板。其进一步特征在于：在制备所述聚氨酯芯材时，向所述聚氨酯芯材中添加原位聚合二乙基次磷酸铝包覆可膨胀石墨作为阻燃剂；所述聚氨酯芯材的具体制备步骤为：按照重量份数计，a、每100份的聚醚多元醇加入稳定剂3～5份、水0.5～1.5份和胺类催化剂1～4份，在1000～1200rpm下搅拌2～3m...
【技术保护点】
1.复合夹心彩钢板，其包括聚氨酯芯材和位于所述聚氨酯芯材外侧的彩钢板基材，其特征在于：所述聚氨酯芯材和所述彩钢板基材之间设有陶瓷纤维板。/n
【技术特征摘要】
1.复合夹心彩钢板，其包括聚氨酯芯材和位于所述聚氨酯芯材外侧的彩钢板基材，其特征在于：所述聚氨酯芯材和所述彩钢板基材之间设有陶瓷纤维板。
2.根据权利要求1所述的复合夹心彩钢板，其特征在于：在制备所述聚氨酯芯材时，向所述聚氨酯芯材中添加原位聚合二乙基次磷酸铝包覆可膨胀石墨作为阻燃剂。
3.根据权利要求2所述的复合夹心彩钢板，其特征在于：所述聚氨酯芯材的具体制备步骤为：按照重量份数计，a、每100份的聚醚多元醇加入稳定剂3～5份、水0.5～1.5份和胺类催化剂1～4份，在1000～1200rpm下搅拌2～3min使之分散均匀；b、向a中的混合物中加入发泡剂10～15份、锡类催化剂0.2～0.5份和作为阻燃剂的原位聚合二乙基次磷酸铝包覆的可膨胀石墨20～30份，在1000～1200rpm下搅拌2～3min使之分散均匀；c、再向b中的混合物中加入120～140份的聚氨酯黑料，在1000～1200rpm下搅拌15～20s后，再将混合物倒入到模具中，待反应和固化完全后，按照所需尺寸...