一种高强度环保瓦楞纸制造技术

本发明专利技术公开了一种高强度环保瓦楞纸,属于造纸技术领域。一种高强度环保瓦楞纸，按照重量份数计配方如下:植物秸秆50‑60份、废纸80‑100份、聚乙烯醇纤维10‑20份、二氧化硅2‑8份、己二酸交联淀粉10‑15份、碳酸钠5‑8份、渗透剂2‑5份。本发明专利技术提供一种高强度环保瓦楞纸，是一种强度高、生产成本低、环保，固体废弃物可资源化利用的瓦楞原纸。

A kind of high strength environmental protection corrugated paper

The invention discloses a high-strength environmental protection corrugated paper, which belongs to the technical field of papermaking. A kind of high-strength environmental protection corrugated paper is formulated according to the weight parts as follows: 50 \u2011 60 parts of plant straw, 80 \u2011 100 parts of waste paper, 10 \u2011 20 parts of polyvinyl alcohol fiber, 2 \u2011 8 parts of silica, 10 \u2011 15 parts of adipic acid cross-linked starch, 5 \u2011 8 parts of sodium carbonate and 2 \u2011 5 parts of penetrant. The invention provides a high-strength environmental protection corrugating paper, which is a corrugating base paper with high strength, low production cost, environmental protection and recyclable solid waste.

【技术实现步骤摘要】
一种高强度环保瓦楞纸
本专利技术属于造纸
，特别涉及一种高强度环保瓦楞纸。
技术介绍
瓦楞纸是由挂面纸和通过瓦楞棍加工而形成的波形的瓦楞纸粘合而成的板状物，一般分为单瓦楞纸板和双瓦楞纸板两类，按照瓦楞的尺寸分为:A、B、C、E、F五种类型。A型楞制成的瓦楞纸板具有较好的缓冲性，富有一定的弹性，C型楞较A型楞次之。但挺度和抗冲击性优于A型楞；B型楞排列密度大，制成的瓦楞纸板表面平整，承压力高，适于印刷；E型楞由于薄而密，更呈现了它的刚强度。瓦楞纸的专利技术和应用有一百多年历史，具有成本低、质量轻、加工易、强度大、印刷适应性样优良、储存搬运方便等优点，80％以上的瓦楞纸均可通过回收再生，瓦楞纸可用作食品或者数码产品的包装，相对环保，使用较为广泛。瓦楞纸箱是由瓦楞纸板制作而成，是使用最广泛的纸容器包装，广泛用于运输包装。瓦楞纸箱之所以应用广泛，是因为它具有许多独特的优点:缓冲性能好；轻便、牢固；外形尺寸小；原料充足，成本低；便于自动化生产；包装作业成本低；能包装多种物品；金属用量少；印刷性能好；可回收复用。通常用作商品的包裹物或物品保护本文档来自技高网...

【技术保护点】
1.一种高强度环保瓦楞纸，其特征在于，所述高强度环保瓦楞纸按照重量份数计配方如下:植物秸秆50-60份、废纸80-100份、聚乙烯醇纤维10-20份、二氧化硅2-8份、己二酸交联淀粉10-15份、碳酸钠5-8份、渗透剂2-5份。/n

【技术特征摘要】
1.一种高强度环保瓦楞纸，其特征在于，所述高强度环保瓦楞纸按照重量份数计配方如下:植物秸秆50-60份、废纸80-...