The invention discloses a radiation resistant and breathable clothing fabric for employees and a preparation method thereof. The clothing includes a base cloth and a radiation resistant layer. The preparation method includes: preparing a coating, applying the coating on the base cloth; heating the base cloth to form a radiation resistant layer, and stretching to form a radiation resistant and breathable clothing fabric for employees; when applying the base cloth, only the bottom surface of the base cloth is applied The coating is applied and dried quickly to prevent the coating from penetrating into the upper surface of the base fabric. The side without coating is used as the lining. The clothing fabric has good radiation resistance and comfortable wearing. The tension roller is used to stretch the base fabric to make the pores on the base fabric open, so as to improve the permeability of the clothing fabric. Only one of the base fabric is applied The graphene in the coating is only covered on one side of the base fabric, so that the clothing fabric has good air permeability.
【技术实现步骤摘要】
一种防辐射透气员工服装面料及其制备方法
本专利技术涉及服装
,尤其涉及一种防辐射透气员工服装面料及其制备方法。
技术介绍
生活中很多工作环境中存在对人体有害的光线,因此需要一种防辐射的员工服装,目前的防辐射服装穿着不舒适,而且透气效果差;专利文件(CN107142720A)提供一种石墨烯防辐射服的制备方法,该方法中通过将布料基层浸渍在分散石墨烯溶液中,使得石墨烯完全填充在布料基层中,对布料基层的纤维孔隙造成封堵,不仅导致该石墨烯防辐射服穿着不舒适,同时导致该防辐射服的透气性能较差,而且二甲基甲酰胺对人体有害,如果没有去除干净存在潜在危险。
技术实现思路
本专利技术的目的在于提供一种防辐射透气员工服装面料及其制备方法,通过涂布电机带动涂布辊转动将涂料槽中的涂料涂抹在基层布料的底面,并通过加热板对基层布料进行加热,使涂料快速烘干并形成防辐射层,同时基层布料在涂抹涂料时仅对基层布料的底面进行了涂抹,并快速对涂料进行烘干,防止涂料渗透到基层布料的上表面,未涂抹涂料的一侧作为衬里,该服装在具有良好防辐射性能的同时也保证了穿着舒适,解决了现有防辐射员工服装穿着不舒适的技术问题;通过摆动气缸带动摆杆转动,从而带动张紧辊下压对基层布料进行拉伸,使得基层布料上的孔隙张开,避免石墨烯对基层布料表面完全封堵,涂抹时仅对基层布料的一面进行涂抹,使得涂料中的石墨烯仅覆盖在基层布料一侧,解决了现有防辐射员工服装透气性差的技术问题。本专利技术的目的可以通过以下技术方案实现:一种防辐射透气员 ...
【技术保护点】
1.一种防辐射透气员工服装面料,其特征在于,包括基层布料(1)和防辐射层(2),该防辐射透气员工服装由下述步骤制备得到:/n步骤一、将20-30份石墨烯粉加入容器中,并加入30-40份去离子水,在500/min的转速下搅拌30min,然后超声分散1-1.5h,加入15-25份水溶性聚氨酯、1-3份硅凝胶,在400/min的转速下搅拌45min,得到涂料,并将涂料加入涂抹装置的涂料槽(7)中;/n步骤二、启动驱动电机(14),驱动电机(14)带动放布辊(8)放料,并通过第三气缸(25)向下推动升降板(23)并使升降辊(6)下降,升降辊(6)推动基层布料(1)与涂布辊(5)紧密接触,启动涂布电机,涂布电机带动涂布辊(5)转动并使涂料槽(7)内的涂料均布于涂布辊(5)的外周面处,并将涂料均匀涂抹到与涂布辊(5)接触的基层布料(1)的底部;/n步骤三、基层布料(1)经过加热板(18)的下方时,启动第一气缸(17),第一气缸(17)带动加热板(18)下降与基层布料(1)的上表面接触并加热,使涂料烘干均匀附着在基层布料(1)的底部形成防辐射层(2);/n步骤四、启动摆动气缸(30),摆动气缸(30 ...
【技术特征摘要】
1.一种防辐射透气员工服装面料,其特征在于,包括基层布料(1)和防辐射层(2),该防辐射透气员工服装由下述步骤制备得到:
步骤一、将20-30份石墨烯粉加入容器中,并加入30-40份去离子水,在500/min的转速下搅拌30min,然后超声分散1-1.5h,加入15-25份水溶性聚氨酯、1-3份硅凝胶,在400/min的转速下搅拌45min,得到涂料,并将涂料加入涂抹装置的涂料槽(7)中;
步骤二、启动驱动电机(14),驱动电机(14)带动放布辊(8)放料,并通过第三气缸(25)向下推动升降板(23)并使升降辊(6)下降,升降辊(6)推动基层布料(1)与涂布辊(5)紧密接触,启动涂布电机,涂布电机带动涂布辊(5)转动并使涂料槽(7)内的涂料均布于涂布辊(5)的外周面处,并将涂料均匀涂抹到与涂布辊(5)接触的基层布料(1)的底部;
步骤三、基层布料(1)经过加热板(18)的下方时,启动第一气缸(17),第一气缸(17)带动加热板(18)下降与基层布料(1)的上表面接触并加热,使涂料烘干均匀附着在基层布料(1)的底部形成防辐射层(2);
步骤四、启动摆动气缸(30),摆动气缸(30)的输出杆伸出并带动摆杆(9)绕转动杆(29)转动,并使张紧辊(10)下压对附着有防辐射层(2)的基层布料(1)进行压紧拉伸,拉伸完成后进行收卷得到防辐射透气员工服装面料。
2.根据权利要求1所述的一种防辐射透气员工服装面料,其特征在于,所述基层布料(1)由聚酯纤维构成。
3.根据权利要求1所述的一种防辐射透气员工服装面料,其特征在于,所述加热板(18)的加热温度为75-105℃。
4.根据权利要求1所述的一种防辐射透气员工服装面料,其特征在于,所述涂抹装置包括底座(3),所述底座(3)的两侧对称固定有两个支撑板(4),两个所述支撑板(4)均固定连接有第二安装板(13),两个所述第二安装板(13)之间设置有放布辊(8),其中一个所述第二安装板(13)上固定安装有驱动电机(14),所述驱动电机(14)的输出轴端与放布辊(8)的一端固定连接,两个所述第二安装板(13)的上方均设置有第一安装板(11),所述第一安装板(11)与支撑板(4)固定连接,两个所述第一安装板(11)之间垂直设置有两个支撑辊(12);
两个所述支撑板(4)之间设置有涂布辊(5)和升降辊(6),所述涂布辊(5)的一端与安装于其中一个支撑板(4)外壁处的涂布电机的输出轴固定连接,所述涂布辊(5)的下方设置有涂料槽(7),所述涂料槽(7)的两端分别与两个支撑板(4)的内壁固定连接;
两个所述支撑板(4)之间还设置有转动杆(29),所述转动杆(29)位于涂料槽(7)的下方,所述转动杆(29)的两端通过轴承分别与两个支撑板(4)的内壁转动连接,所述转动杆(29)上固定连接有两个摆杆(9),两个所述摆杆(9)呈对称分布,且两个所述摆杆(9)远离转动杆(29)的端部之间转动连接有张紧辊(10),两个所述支撑板(4)的内壁处分别铰接有摆动气缸(30),所述摆动气缸(30)的一端与摆杆(9)的中部铰接;
两个所述支撑板(4)之间固定安装有第一横杆(15)和第二横杆(16),所述第二横杆(16)靠近第一横杆...