The invention belongs to the field of nano material preparation, in particular to a green, fast and low-cost silk nanofiber preparation method. The natural cocoon was added to the aqueous solution of strong alkali and mixed. The mixture was immersed at 1 \u2011 500r / s and 4 \u2011 95 \u2103 for 0.1 \u2011 100h. After centrifugal washing and ultrasonic dispersion, the high yield, diameter distribution of 2 \u2011 28nm and length distribution of 100 \u2011 3000Nm were obtained. The invention has the advantages of simple operation, low production cost, environmental protection, short production cycle, no large-scale instrument and equipment, and can realize large-scale industrialized preparation of silk nanofibers.
【技术实现步骤摘要】
一种快速、低成本制备蚕丝纳米纤维的方法
本专利技术属于纳米材料制备领域，具体涉及一种绿色、快速、低成本的蚕丝纳米纤维制备方法。
技术介绍
蚕丝纳米纤维具有生物相容性好、绿色可降解、来源广泛、力学性能优异等优点，是开发先进光学材料、可植入机体的生物材料、高性能复合材料的重要研究对象。为制备蚕丝纳米纤维，从天然蚕丝纤维中“自上而下”地剥离出蚕丝纳米纤维是一种常用的方法。这类方法通常是利用有机溶剂或强酸、高盐溶液将蚕丝纤维不完全溶解或水解，以破坏丝素蛋白内部分子间相互作用力，从而获得蚕丝微纳米纤维；或借助超声破碎等机械手段将蚕丝微纳米纤维从本体粗纤维上直接剥离。然而，上述方法通常面临能耗高、制备过程复杂、使用有毒有害溶剂等问题，且剥离得到的蚕丝纳米纤维的尺寸分布不均匀、稳定性差。通过对现有蚕丝纳米纤维制备技术文献和专利的检索发现,中国专利文献号CN104532365B，公开日期2016年4月27日，公开了一种蚕丝微纳米纤维的制备方法，该方法首先将蚕丝纤维浸泡在无机盐或弱酸或弱碱溶液中，以减弱蚕丝纳米原纤间的结合力，之后利用...
【技术保护点】
1.一种快速、低成本制备蚕丝纳米纤维的方法，其特征在于：将天然蚕茧加至强碱的水溶液中混合，混合液在1-500r/s的搅拌速度、4-95℃温度下浸泡0.1-100h，离心洗涤、超声分散获得高产率、直径分布为2-28nm，长度分布为100-3000nm蚕丝纳米纤维的分散液。/n
【技术特征摘要】
1.一种快速、低成本制备蚕丝纳米纤维的方法，其特征在于：将天然蚕茧加至强碱的水溶液中混合，混合液在1-500r/s的搅拌速度、4-95℃温度下浸泡0.1-100h，离心洗涤、超声分散获得高产率、直径分布为2-28nm，长度分布为100-3000nm蚕丝纳米纤维的分散液。
2.按权利要求1所述的快速、低成本制备蚕丝纳米纤维的方法，其特征在于：所述混合液优选在20-100r/s的搅拌速度、15-40℃温度下，浸泡12-24h，用去离子水在4000-6000rpm离心洗涤、超声分散获得蚕丝纳米纤维的分散液。
3.按权利要求1或2所述的快速、低成本制备蚕丝纳米纤维的方法，其特征在于：所述混合液中蚕茧的终浓度为0.01-10wt.％，强碱的水溶液浓度为0.1-20wt.％。
4.按权利要求3所述的快速、低成本制备蚕丝纳米纤维的方法，其特征在于：所述强碱的水溶液是无机强...