The invention discloses a preparation method of lithium battery membrane, which is composed of the following steps: (1) immersing bacterial cellulose membrane in an aqueous solution containing crosslinking agent for 12-48 hours; the crosslinking agent is at least one of formaldehyde, glutaraldehyde and butanedialdehyde; (2) placing the wet film obtained in step (1) in a freeze dryer for freeze drying; (3) immersing step The dry film obtained in step (2) is dried in a vacuum oven at 50 \u2011 120 \u2103 to obtain a lithium battery membrane. Compared with the existing bacterial cellulose membrane, the preparation method of the invention can reduce the side reaction between the membrane and lithium metal, the prepared lithium battery has longer cycle life and higher coulomb efficiency, thus realizing the purpose of lithium metal negative pole protection.
【技术实现步骤摘要】
一种锂电池隔膜的制备方法(一)
本专利技术属于新能源材料
，涉及一种锂电池隔膜的制备方法。(二)
技术介绍
金属锂作为电极的锂电池广泛应用于便携式电子、电器、电动汽车和电网规模的能源储存系统。因此，开发低成本、生态高效、环境友好的锂电池产品是非常可取的，以保持可持续性的大规模使用未来可再生能源。隔膜是锂电池的重要组成部分。对其安全性、使用寿命和电化学性能有较大影响，对于能源存储系统的可持续性也非常重要。一方面，隔膜作为阳极和阴极之间的电子隔离层，要避免内部短路，这就要求绝缘性能高、机械强度，电化学和热稳定性好。另一方面，隔膜为锂离子在两个电极之间的迁移提供了通道，要求在液体中具有良好的导锂离子能力。目前，聚烯烃隔膜如聚乙烯、聚丙烯由于其性能优良、绝缘性能好、机械强度高、电化学稳定性好，在工业生产中得到了广泛的应用。然而，聚烯烃隔膜，从有限的石油得到，并不满足生态高效、环境友好、可持续的要求。此外，其热稳定性差严重影响锂电池的安全性和使用寿命。因此，许多原材料被研究用以替代聚烯烃基隔膜，如聚丙烯腈，聚酰亚胺、聚邻苯二甲酸...
【技术保护点】
1.一种锂电池隔膜的制备方法，其特征在于：所述制备方法由如下步骤组成：/n(1)将细菌纤维素膜浸泡于含有交联剂的水溶液中，浸泡时间12-48小时；所述的交联剂为甲醛、戊二醛、丁二醛中的至少一种；/n(2)将步骤(1)所得的湿膜置于冷冻干燥机中进行冷冻干燥；/n(3)将步骤(2)所得的干燥膜，置于50-120℃真空烘箱烘干，得到锂电池隔膜。/n
【技术特征摘要】
1.一种锂电池隔膜的制备方法，其特征在于：所述制备方法由如下步骤组成：
(1)将细菌纤维素膜浸泡于含有交联剂的水溶液中，浸泡时间12-48小时；所述的交联剂为甲醛、戊二醛、丁二醛中的至少一种；
(2)将步骤(1)所得的湿膜置于冷冻干燥机中进行冷冻干燥；
(3)将步骤(2)所得的干燥膜，置于50-120℃真空烘箱烘干，得到锂电池隔膜。
2.如权利要...
【专利技术属性】
技术研发人员：陶新永，陈媚，盛欧微，金成滨，袁华栋，居治金，刘铁锋，佴建威，王垚，刘育京，
申请(专利权)人：浙江工业大学，
类型：发明
国别省市：浙江;33