The invention discloses a chlorella covered by polydopamine and a preparation method thereof. The invention uses dopamine to modify Chlorella and synthesize different kinds of Chlorella wrapped by polydopamine, which can solve a variety of environmental problems. The specific applications of the multifunctional Chlorella include: (1) highly effective adsorption of heavy metal ions in water; (2) in situ adsorption and accumulation of oil in water; (3) fluorescence detection of pollutants. Chlorella, as a kind of biomaterial, widely exists in the natural environment, and polydopamine is also a kind of biopolymer similar to mussel adhesion protein, so the synthesized multifunctional Chlorella has the characteristics of environmental protection. The synthesis process is simple and efficient, and the raw materials used are cheap, which can be widely used in practice.
【技术实现步骤摘要】
一种聚多巴胺包覆的小球藻及其制备方法
本专利技术属于微纳米材料及环境领域，具体涉及一种聚多巴胺包覆的小球藻，以及包覆和修饰的制备方法。
技术介绍
近年来，水污染急剧加速，已经大大阻碍了社会的可持续发展，也引发重大的环境和人类健康问题。目前，水污染是世界上主要的死亡原因之一，每年造成200万人死亡。如何解决水污染问题，是实现可持续发展面临的一个重要问题。去除和分离水中污染物的方法主要有化学沉淀法、吸附法、离子交换法、溶剂萃取法、氧化还原法等。吸附法由于其简单易行的特点，得到了广泛的应用，多年来，各种吸附剂包括无机材料、聚合物、木材废弃物、碳基材料等都被研究用于处理水污染。微纳米环境功能材料由于其多种优异特性是目前研究的一个重点。微纳米材料有两个关键特性，使它们作为吸附剂特别具有吸引力:(1)它们的表面积在质量基础上比体积粒子大得多；(2)它们还可以进行多种功能化，以增强它们对特定化合物的亲和力。因此，这种方法对去除低浓度污染物特别有效。因此，制备简单、环保、能有效去除污染物的新型纳米材料是非常必要的。聚多巴胺(PDA)...
【技术保护点】
1.一种聚多巴胺包覆的小球藻，其特征在于，其内核是小球藻，外层包覆层是聚多巴胺。/n
【技术特征摘要】
1.一种聚多巴胺包覆的小球藻，其特征在于，其内核是小球藻，外层包覆层是聚多巴胺。
2.根据权利要求1所述的聚多巴胺包覆的小球藻，其特征在于，所述的包覆层内还含有碳量子点。
3.根据权利要求1所述的聚多巴胺包覆的小球藻，其特征在于，所述的包覆层外修饰有铁的氧化物。
4.根据权利要求1所述的聚多巴胺包覆的小球藻，其特征在于，所述的聚多巴胺采用以下方法包覆：将重量比例为1:2的小球藻和盐酸多巴胺放入pH8.5的Tris-HCl缓冲溶液中，搅拌10～20h，离心，烘干。
5.根据权利要求2所述的聚多巴胺包覆的小球藻，其特征在于，所述的碳量子点采用以下方法包覆：将碳量子点与盐酸多巴胺放入pH8.5的Tris缓冲溶液中，搅拌10～20h，离心，沉积物与小球藻按2:1的比例放入pH8.5的Tris缓冲溶液中，再搅拌10～20h，离心，烘干。
6.根据权利要求3所述的聚多巴胺包覆的小球藻，其特征在于，所述的铁的氧化物的复合方法是：将小球藻分散于去离子水中，在搅拌中加入FeCl2和FeCl3混合溶液，再加入氨水，24h后，离心，烘干。
<...
【专利技术属性】
技术研发人员：王虹，潘思好，王珂，
申请(专利权)人：中国矿业大学，
类型：发明
国别省市：江苏;32