The invention discloses a dental resin material, which is composed of the following components according to the mass percentage: 20-30% hydroxy calcium phosphate, 10-15% methyl polyacrylate, 5-10% triethyl citrate, 5-10% diethyl dodecyl phosphonate, 10-15% calcium alginate, 2-8% antibacterial agent, 5-10% antioxidant, 1-3% stabilizer and 20-25% double distilled water The sum of the percentage by mass is 100%. The invention also specifically discloses the preparation method of the resin material for filling teeth; the resin material for filling teeth prepared by the invention has good compressive strength and hardness, and does not contain heavy metals, is environmentally friendly, the preparation method is simple and convenient, and is easy to promote.
【技术实现步骤摘要】
一种补牙用树脂材料及其制备方法
本专利技术属于牙齿修复领域，具体涉及一种补牙用树脂材料，还涉及上述补牙用树脂材料的制备方法。
技术介绍
牙齿是人类非常重要的器官。龋齿又称为虫牙或者蛀牙，是一种细菌性疾病，是牙齿发生腐蚀的病变，在牙面上形成的一种龋洞，龋洞会越来越大，可使牙齿完全破坏，龋齿如果不进行治疗的话，最终会使得牙冠完全破坏消失，不能咀嚼东西。治疗龋齿的方法主要采用补牙材料进行填充，即先将坏掉的龋齿清除干净，利用工具作出一定的形状，将补牙材料进行填充并回复牙齿缺损的外形，目前常采用的银汞合金、复合树脂，由于银汞合金中汞有毒，所以现在常用的补牙材料为树脂材料，树脂与银汞合金填充材料相比，具备优良的生物相容性、机械、美观等性能，已成为目前各种牙科组织损伤的主要方式，但是由于牙科树脂在使用的过程中容易受到磨损，导致龋齿修复位置再次出现龋齿的症状，所以，发展一种使用寿命长、体积不容易收缩的新型树脂材料很有必要。
技术实现思路
本专利技术的目的在于提供一种补牙用树脂材料，具有使用寿命长、硬度大的特点。<...
【技术保护点】
1.一种补牙用树脂材料，其特征在于，按照质量百分比由以下组分组成：羟基磷酸钙20～30％，聚丙烯酸甲酯10～15％，枸橼酸三乙酯5～10％，十二烷基膦酸二乙基酯5～10％，海藻酸钙10～15％，抗菌剂2～8％，抗氧化剂5～10％，稳定剂1～3％，双蒸水20～25％，以上各组分的质量百分比之和为100％。/n
【技术特征摘要】
1.一种补牙用树脂材料，其特征在于，按照质量百分比由以下组分组成：羟基磷酸钙20～30％，聚丙烯酸甲酯10～15％，枸橼酸三乙酯5～10％，十二烷基膦酸二乙基酯5～10％，海藻酸钙10～15％，抗菌剂2～8％，抗氧化剂5～10％，稳定剂1～3％，双蒸水20～25％，以上各组分的质量百分比之和为100％。
2.根据权利要求1所述一种补牙用树脂材料，其特征在于，所述抗菌剂为纳米银粉及苦参总碱粉末混合物，其苦参总碱粉末与纳米银粉的质量比为1:1～3。
3.根据权利要求2所述一种补牙用树脂材料，其特征在于，所述纳米银粉的粒径范围为50～100nm。
4.根据权利要求3所述一种补牙用树脂材料，其特征在于，所述纳米银粉的粒径为50～60nm。
5.根据权利要求1所述一种补牙用树脂材料，其特征在于，所述稳定剂为对甲氧基酚。
6.根据权利要求1所述一种补牙用树脂材料，其特征在于，所述抗氧化剂为邻甲氧基苯酚。
7.一种补牙用树脂材料的制备方法，其特征在于，按照以下具体步骤实施：
步骤1、按照重量分别称取羟基磷酸钙20～30％，聚丙烯酸甲酯10～15％，枸橼酸三乙...
【专利技术属性】
技术研发人员：张耀超，左艳萍，张琳梅，崔晓明，
申请(专利权)人：西安医学院，
类型：发明
国别省市：陕西;61