The invention provides a preparation method of graphene antibacterial fabric, which comprises the following steps: S1. Coating the fabric surface after evenly mixing the antibacterial agent and the adhesive, and then drying; S2. Putting the dried fabric into the mixed solution of reducing agent and deionized water for reduction treatment, and then taking out the fabric for drying; the antibacterial agent is graphene, graphene oxide, amino modified One or more of graphene. The invention adopts a new type of graphene antibacterial raw material combined with adhesion and chemical combination to realize the antibacterial function on the single-layer fabric, which ensures the antibacterial performance and washing fastness of the fabric, and improves the antibacterial and washing resistance of the fabric.
【技术实现步骤摘要】
一种石墨烯抗菌面料及其制备方法
本专利技术涉及抗菌涂料领域，具体地，涉及一种石墨烯抗菌面料及其制备方法。
技术介绍
抗菌面料具有良好的安全性，它可以高效完全去除织物上的细菌、真菌和霉菌，保持织物清洁，并能防止细菌再生和繁殖。传统抗菌面料采用抗菌剂后整理到织物表面，其缺点是，采用银离子等抗菌剂现已全面禁用，而有机类的抗菌剂效果不好，牢度差，耐洗行不好。目前面料上的抗菌问题，主要需解决：1、面料使用的抗菌剂牢度不好，耐洗性差；2、使用涂层透气性不好的问题。因此，如何获得一种抗菌性高、牢度好、透气性佳的面料是目前亟需解决的问题。公开为CN107629663A公开了一种石墨烯涂料及其制备方法，该石墨烯涂料的配方按重量份数包括：胶粘剂20～50份，固含量0.3～8％的石墨烯分散液2～15份，表面活性剂0.01～0.5份，去离子水5～20份；该石墨烯涂料涂布成膜后具有极高的硬度、极低的阻抗和高性能的隔热性、抗划伤能力强，自洁能力好，隔热保温效果更强的特点。但该专利由于只采用胶黏剂粘合，存在牢度不好的缺点，不耐水洗牢度。<...
【技术保护点】
1.一种石墨烯抗菌面料的制备方法，其特征在于，包括如下步骤：/nS1、将抗菌剂和粘合剂均匀混合后涂覆在织物表面，然后烘干；/nS2、将烘干后的织物放入还原剂和去离子水的混合溶液中进行还原处理，然后取出织物烘干；/n所述抗菌剂为石墨烯、氧化石墨烯、氨基改性石墨烯中的一种或几种。/n
【技术特征摘要】
1.一种石墨烯抗菌面料的制备方法，其特征在于，包括如下步骤：
S1、将抗菌剂和粘合剂均匀混合后涂覆在织物表面，然后烘干；
S2、将烘干后的织物放入还原剂和去离子水的混合溶液中进行还原处理，然后取出织物烘干；
所述抗菌剂为石墨烯、氧化石墨烯、氨基改性石墨烯中的一种或几种。
2.根据权利要求1所述的石墨烯抗菌面料的制备方法，其特征在于，步骤S1和步骤S2中，所述烘干的温度为60℃-80℃。
3.根据权利要求1所述的石墨烯抗菌面料的制备方法，其特征在于，步骤S2中，所述还原处理的温度为80℃，时间为60-90min。
4.根据权利要求1所述的石墨烯抗菌面料的制备方法，其特征在于，所述抗菌剂、粘合剂、还原剂和去离子水的质量比为(0.1～1.5)：(4.6～6)：(2.6～4)：(88.5～89.9)。
5.根据权利要求1所述的石墨烯抗菌面料的制备方法，其特征在于，所述氨基改性石墨烯的表面带有氨基基团，所述氨基基团的质量占所述氨基改性石墨烯质量的10-20...
【专利技术属性】
技术研发人员：沙嫣，沙晓林，
申请(专利权)人：南通强生石墨烯科技有限公司，
类型：发明
国别省市：江苏;32