The present invention relates to an electronic wiring harness protective sleeve with fire-proof performance. Its characteristics are as follows: ethylene glycidyl methacrylate 30 40 phr, butadiene succinate 20 30 phr, glass fiber 10 15 phr, ethylene propylene terpolymer 5 10 phr, basalt fiber 5 10 phr, flame retardant 0.2 phr. 0.4 phr, 0.1 phr, 0.4 phr of vulcanizing agent, 0.5 phr of antioxidant, 0.2 phr of heat stabilizer, 0.6 phr of sodium allyl sulfonate, 0.2 phr of ethanol and 10 phr of ethanol. The invention has good fire protection performance, effectively prolongs the service life of the electronic wiring harness, and ensures the stability and persistence of the power supply and signal for the transmission of the electronic wiring harness.
【技术实现步骤摘要】
一种具有防火性能的电子线束保护套
本专利技术涉及电子线束
,尤其涉及一种具有防火性能的电子线束保护套。
技术介绍
线束是运载设备之间来往的信号和电源的连接,是电路中连接各电器设备的接线部件,电子线束用来传递电子元器件之间的信号和电源,传统的电子线束在安装和使用时,线束直接暴露在外部,在潮湿环境,很容易导致电子线束受潮,传输信号和电源不稳定或者无法传递,同时由于电子线束使用场合的特殊性,很容易产生静电,吸收灰尘,造成污染,当外部温度过高时,高温容易烧毁电子线束,造成线束无法正常使用,或者导致电子线束的使用寿命降低的问题,因此需要对电子线束进行保护,延长其使用寿命,从而保证电子线束的正常使用。
技术实现思路
为解决上述问题,本专利技术提供了一种具有防火性能的电子线束保护套。本专利技术的技术方案如下:一种具有防火性能的电子线束保护套,其特征在于:所述具有防火性能的电子线束保护套的组分按照重量份如下所示:乙烯-甲基丙烯酸缩水甘油酯30-40份、烯基丁二酸酯20-30份、玻璃纤维10-15份、三元乙丙橡胶5-10份、玄武岩纤维5-10份、阻燃剂0.2-0.4份、硫化剂0.1-0.4份、抗氧化剂0.5-1份、热稳定剂0.2-0.6份、烯丙基磺酸钠0.2-0.5份和乙醇10-20份。进一步的,所述阻燃剂为三聚氰胺、磷酸三苯酯和甲苯基二苯基磷酸酯中的一种或几种混合。进一步的,所述硫化剂为N,N’-间苯撑双马来酰亚胺。进一步的,所述抗氧化剂为四(3,5-二叔丁基-4-4羟苯基)。进一步的,所述热稳定剂为二盐基邻苯二甲酸铅。借由上述方案,本专利技术至少具有如下优点:本专利技 ...
【技术保护点】
1.一种具有防火性能的电子线束保护套,其特征在于:所述具有防火性能的电子线束保护套的组分按照重量份如下所示:乙烯‑甲基丙烯酸缩水甘油酯30‑40份、烯基丁二酸酯20‑30份、玻璃纤维10‑15份、三元乙丙橡胶5‑10份、玄武岩纤维5‑10份、阻燃剂0.2‑0.4份、硫化剂0.1‑0.4份、抗氧化剂0.5‑1份、热稳定剂0.2‑0.6份、烯丙基磺酸钠0.2‑0.5份和乙醇10‑20份。
【技术特征摘要】
1.一种具有防火性能的电子线束保护套,其特征在于:所述具有防火性能的电子线束保护套的组分按照重量份如下所示:乙烯-甲基丙烯酸缩水甘油酯30-40份、烯基丁二酸酯20-30份、玻璃纤维10-15份、三元乙丙橡胶5-10份、玄武岩纤维5-10份、阻燃剂0.2-0.4份、硫化剂0.1-0.4份、抗氧化剂0.5-1份、热稳定剂0.2-0.6份、烯丙基磺酸钠0.2-0.5份和乙醇10-20份。2.根据权利要求1所述的一种具有防火性能的电子...
【专利技术属性】
技术研发人员:刘云鹏,
申请(专利权)人:常州德瑞电子有限公司,
类型:发明
国别省市:江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。