The invention provides a geological polymer tunnel flame retardant coating, which is composed of 36-43 copies of geological polymer, 11-16 copies of polyvinyl chloride, 18-28 copies of perchloroethylene, 13-16 copies of brucite fiber, 3-5 copies of chlorinated rubber, 3-5 copies of hydroxymethyl cellulose and 0.03-0.05 copies of aliphatic alcohol sulfonate air entraining agent, in which the geological polymer is made of heavy weight. Unit of measure, consist of 18 parts of Taibai powder, 11 parts of kaolin, 3 parts of calcium bentonite, 5 parts of calcium oxide, 11 parts of sodium carbonate, 2 parts of alumina, 3 parts of sodium sulfate and 50 parts of asbestos powder. The geological polymer binder used in the invention has the characteristics of low material source cost, high bonding strength, excellent fire resistance and durability; the tunnel flame retardant coating of the invention has the characteristics of long fire resistance limit time, high bonding strength and excellent freeze-thaw resistance, and is a tunnel flame retardant coating with good performance.
【技术实现步骤摘要】
一种地质聚合物隧道阻燃涂料
本专利技术属于阻燃涂料领域，涉及一种隧道阻燃涂料，具体涉及一种地质聚合物隧道阻燃涂料。
技术介绍
隧道阻燃涂料是专门针对隧道墙壁和拱顶在火灾中免受烧损而专门设计的一种专用阻燃涂料。当前，我国隧道阻燃涂料生产厂家众多，基本上都是以高铝水泥为粘结剂，聚氯乙烯、过氯乙烯等轻质骨料，配合而成隧道阻燃涂料，典型的问题是该类隧道阻燃涂料粘结强度低，涂层薄阻燃等级低，涂层厚易脱落，阻燃涂层装饰性差。
技术实现思路
针对现有技术中存在的不足，本专利技术的目的在于，提供一种地质聚合物隧道阻燃涂料及其制备方法。为了实现上述任务，本专利技术采用如下技术方案予以实现：一种地质聚合物隧道阻燃涂料，以重量单位计，由以下原料组成：地质聚合物36～43份，聚氯乙烯11～16份，过氯乙烯18～28份，水镁石纤维13～16份，氯化橡胶3～5份，羟甲基纤维素3～5份，脂肪醇磺酸盐引气剂0.03～0.05份，其中：所述的地质聚合物，以重量单位计，由以下原料组成：太白粉18份，高岭土11份，钙基膨润土3份，氧化钙5份，碳酸钠11份，氧化铝2份，硫酸钠3份，石棉粉50份。本专利技术还...
【技术保护点】
1.一种地质聚合物隧道阻燃涂料，其特征在于，以重量单位计，由以下原料组成：地质聚合物36～43份，聚氯乙烯11～16份，过氯乙烯18～28份，水镁石纤维13～16份，氯化橡胶3～5份，羟甲基纤维素3～5份，脂肪醇磺酸盐引气剂0.03～0.05份，其中：所述的地质聚合物，以重量单位计，由以下原料组成：太白粉18份，高岭土11份，钙基膨润土3份，氧化钙5份，碳酸钠11份，氧化铝2份，硫酸钠3份，石棉粉50份。
【技术特征摘要】
1.一种地质聚合物隧道阻燃涂料，其特征在于，以重量单位计，由以下原料组成：地质聚合物36～43份，聚氯乙烯11～16份，过氯乙烯18～28份，水镁石纤维13～16份，氯化橡胶3～5份，羟甲基纤维素3～5份，脂肪醇磺酸盐引气剂0.03～0.05份，其中：所述的地质聚...