The present invention relates to a treatment method of tin-containing sludge, which includes the following steps: mixing tin-containing sludge with pure water to obtain slurry; separating the slurry from solid-liquid to obtain filtrate and solid phase; heat treating the solid phase to obtain tin oxide products; filtering the filtrate to obtain water and filter residue, and reusing the water produced in the equipment as pure water. When the concentration of the concentrated solution reaches a certain level, the electroplating solution is selected to be returned to production or put into the incinerator according to the specific conditions. The invention has the following beneficial effects: compared with the existing technology, the beneficial effects of the invention are: 1. full quantification of hazardous waste disposal; 2. low energy consumption and zero emission of the whole process; 3. simple process, conducive to commercialization.
【技术实现步骤摘要】
一种含锡污泥的处理方法
本专利技术属于环保
，特别是提供了一种对电镀过程产生的含锡污泥的资源化处置方法。
技术介绍
含锡污泥主要在电镀锡产线产生，pH值在3～4左右，污泥中含有PSA有机酸，属于国家危险废弃物类别HW17，其中主要需处理的污染物指标为：有机酸PSA(不同的企业采用不相同的电镀液配方，对于酸的选择也不太相同)和锡、铁、铅等金属的氧化物。含锡污泥由于是危险废弃物，处理工艺较为复杂，目前市场上对含锡污泥的处理一般是进入冶炼炉，对设备腐蚀严重，能耗高。
技术实现思路
本专利技术的目的是提供一种对电镀锡企业产生的含锡污泥的处理方法。本专利技术是通过以下技术方案实现的：本专利技术提供了一种含锡污泥的处理方法，其包括如下步骤：将含锡污泥与纯水混合，得到泥浆；将所述泥浆进行固液分离，得到滤液和固相物；将所述固相物进行热处理，得到氧化锡产品；将所述滤液进行过滤后，得到产水和浓液，将产水作为纯水回用，将所述浓液进行收集后用于配制电镀液或进炉焚烧。其中，产水的理化指标如表1所示，浓液的理化指标如表2所示，固相物的理化指标如表3所示。表1表2表3NO元素含量(％)1Sn...
【技术保护点】
1.一种含锡污泥的处理方法，其特征在于，包括如下步骤：将含锡污泥与纯水混合，得到泥浆；将所述泥浆进行固液分离，得到滤液和固相物；将所述固相物进行热处理，得到氧化锡产品；将所述滤液进行过滤后，得到产水和浓液，将产水作为纯水回用，将所述浓液进行收集后用于配制电镀液或进炉焚烧。
【技术特征摘要】
1.一种含锡污泥的处理方法，其特征在于，包括如下步骤：将含锡污泥与纯水混合，得到泥浆；将所述泥浆进行固液分离，得到滤液和固相物；将所述固相物进行热处理，得到氧化锡产品；将所述滤液进行过滤后，得到产水和浓液，将产水作为纯水回用，将所述浓液进行收集后用于配制电镀液或进炉焚烧。2.如权利要求1所述的含锡污泥的处理方法，其特征在于，所述泥浆的固含量为1～20％。3.如权利要求1所述...
【专利技术属性】
技术研发人员：钟伟，许澧鸣，金芳，秦玉敏，季雯赟，何晓燕，
申请(专利权)人：宝武集团环境资源科技有限公司，
类型：发明
国别省市：上海,31