一种喷涂型钢丝绳表面脂组合物及制备方法技术

本发明专利技术涉及一种可用于喷涂作业的钢丝绳表面脂组合物及制备方法。组合物的成分和百分含量如下：普通钢丝绳表面脂25.0％～67.0％；黏附性改进剂1.4％～5.2％；助分散剂1.2％～5.4％；稀释剂5.3％～13.4％；润湿流平剂0.1％～1.0％；气雾推进剂25.0％～50.0％。所得产品气味低，脂膜光滑、均匀、平整,具有良好的黏附性、抗盐雾性、耐低温性和减磨性。特别适用于运行中或维护保养时钢丝绳的润滑和防护。

A Surface Lipid Composition of Spraying Steel Wire Rope and Its Preparation Method

The invention relates to a surface lipid composition of steel wire rope for spraying operation and a preparation method thereof. The composition and percentage content of the composition are as follows: surface grease of ordinary steel rope 25.0%-67.0%; adhesion modifier 1.4%-5.2%; dispersant 1.2%-5.4%; diluent 5.3%-13.4%; wetting leveller 0.1%-1.0%; aerosol propellant 25.0%-50.0%. The obtained product has low odor, smooth, uniform and smooth lipid film, good adhesion, salt spray resistance, low temperature resistance and abrasion reduction. Especially suitable for lubrication and protection of wire rope in operation or maintenance.

【技术实现步骤摘要】
一种喷涂型钢丝绳表面脂组合物及制备方法
本专利技术属于润滑脂
，特别涉及一种可用于喷涂作业的钢丝绳表面脂组合物及制备方法。
技术介绍
普通钢丝绳表面脂外观呈半固体状，主要用于涂覆工程机械、港口机械、矿山机械、电梯等机械设备的钢丝绳表面，起到润滑和防护作用。钢丝绳的涂覆，在钢丝绳生产企业是利用加热装置将表面脂加热至110～140℃温度下融化至流体，然后通过喷涂、浸涂等方式，再使表面脂涂覆于钢丝绳表面。上述涂脂方式，适合于钢丝绳在批量加工过程中，且具备大型加热装置的生产现场实施操作。钢丝绳作为起重、吊装的承重材料，对于机械设备的安全运行十分重要的作用。其中强化使用中的润滑管理、弥补运转时润滑缺陷是克服钢丝绳出现断丝、变形、磨损等事故的重要手段。各类机械设备所配置的钢丝绳，长度从几十米到数百米甚至更长，钢丝绳在使用运转中需要定期维护保养。若仅仅是局部缺少润滑材料时，使用普通钢丝绳表面脂因呈半固体状而无法实现涂覆操作，而采用将其加热融化后涂覆在现场又缺少必要的条件及措施，同时也极易造成烫伤等安全事故。同时，因机械设备庞大在高空或狭窄区域作业，进行涂覆操作也十分不便利。对于工程机械、港口本文档来自技高网...

【技术保护点】
1.一种喷涂型钢丝绳表面脂组合物，其特征是各组分及百分含量为：

【技术特征摘要】
1.一种喷涂型钢丝绳表面脂组合物，其特征是各组分及百分含量为：2.权利要求1所述的一种喷涂型钢丝绳表面脂，其特征是以组合物总重为基准，各组分百分含量：3.如权利要求1或2所述的组合物，其特征是所述普通钢丝绳表面脂要求滴点≥65℃。4.如权利要求1或2所述的组合物，其特征是所述黏附型改进剂由丙烷沥青和苯乙烯-乙烯/丁二稀-苯乙烯嵌段共聚物组成，两者混合比例为9:1～6:4,其中丙烷沥青要求软化点≥65℃，苯乙烯-乙烯/丁二稀-苯乙烯嵌段共聚物要求要求软化点≥95℃。5.如权利要求1或2所述的组合物，其特征是所述助分散剂是由司苯-80和碱性重烷基苯磺酸钙组成，两者混合比例为7:3～5:5,其中司苯-80要求酸值≤8mgKOH/g,碱性重烷基苯磺酸钙要求碱值≥200mgKOH/g。6.如权利要求1或2所述的组合物，其特征是...

【专利技术属性】
技术研发人员：王先会，张军，陈秀建，刘坤，
申请(专利权)人：中国石油化工股份有限公司，
类型：发明
国别省市：北京,11