The invention provides a water-borne super hard baking paint and its preparation method. The system is made up of the following weight groups: silicone modified epoxy emulsion 35~55 parts, amino resin 15~20 parts, hollow glass powder 4~15 parts, titanium white powder 15~20 parts, coating auxiliaries 3~10 parts and distilled water 5~8 parts. The water-borne super hard baking paint and its preparation method are cross-linked by baking silicone modified epoxy emulsion, amino resin, titanium dioxide and hollow glass powder at 160 to 200 degrees Celsius, so as to improve the hardness of one component waterborne baking varnish and take the forward impact into account.
【技术实现步骤摘要】
一种水性超硬烤漆及其制备方法
本专利技术属于水性超硬烤漆制备
，尤其是涉及一种水性超硬烤漆及其制备方法。
技术介绍
烤漆，在家具制造中新兴的一种喷漆制作方法(工艺)。其方法是：在打磨到一定粗糙程度的基底上(通常是高密度板材)，喷上若干层油漆。并经高温烘烤定型。该工艺目前对油漆要求较高，显色性好。烤漆分为两大类，一类低温烤漆固化温度为140℃-180℃，另外一类就称为高温烤漆，其固化温度为280℃-400℃。传统单组份水性烤漆硬度一般在2～3H左右，如何提高单组份水性烤漆硬度，可以通过什么方法将单组份水性烤漆硬度提高到8H，并且能兼顾正向冲击超过50cm/kg的要求。
技术实现思路
有鉴于此，本专利技术旨在提出一种水性超硬烤漆及其制备方法，以提高单组份水性烤漆硬度，并且能兼顾正向冲击的目的。为达到上述目的，本专利技术的技术方案是这样实现的：一种水性超硬烤漆，由以下重量份的组分配制而成：有机硅改性环氧乳液35～55份氨基树脂15～20份空心玻璃粉4～15份钛白粉15～20份涂料助剂3～10份蒸馏水5～8份；所述涂料助剂包括消泡剂A0.1～0.8份、消泡剂B0.1～0...
【技术保护点】
1.一种水性超硬烤漆，其特征在于：由以下重量份的组分配制而成：有机硅改性环氧乳液 35～55份氨基树脂 15～20份空心玻璃粉 4～15份钛白粉 15～20份涂料助剂 3～10份蒸馏水 5～8份；所述涂料助剂包括消泡剂A 0.1～0.8份、消泡剂B 0.1～0.8份、润湿分散剂1.5～6份、基材润湿剂0.1～0.8份、流平剂0.2～1.6份。
【技术特征摘要】
1.一种水性超硬烤漆，其特征在于：由以下重量份的组分配制而成：有机硅改性环氧乳液35～55份氨基树脂15～20份空心玻璃粉4～15份钛白粉15～20份涂料助剂3～10份蒸馏水5～8份；所述涂料助剂包括消泡剂A0.1～0.8份、消泡剂B0.1～0.8份、润湿分散剂1.5～6份、基材润湿剂0.1～0.8份、流平剂0.2～1.6份。2.根据权利要求1所述的一种水性超硬烤漆，其特征在于：所述有机硅改性环氧乳液，其中有机硅含量为5～8％，优选奥洛奇化工的LY-782Z。3.根据权利要求1所述的一种水性超硬烤漆，其特征在于：所述氨基树脂是一种含有异丁醇溶剂的甲基醚化高亚氨基三聚氰胺交联剂。4.根据权利要求1所述的一种水性超硬烤漆，其特征在于：所述钛白粉的粒径分布在40～50μm，80～90μm和2～3μm。5.根据权利要求1所述的一种水性超硬烤漆，其特征在于：所述空心玻璃粉其粒径在2～3μm。6.根据权利要求4所述的一种水性超硬烤漆，其特征在于：所述钛白粉优选龙蟒钛...
【专利技术属性】
技术研发人员：张景明，赵阳，宋士成，张超一，
申请(专利权)人：宝骏新兴建材天津有限公司，
类型：发明
国别省市：天津,12